Effect of Delayed Dentin Sealing versus Immediate Dentin Sealing on Tensile Bond Strength of Ceramic Restoration Material. -An in vitro study- | ||||
| Al-Azhar Journal of Dental Science | ||||
| Article 3, Volume 24, Issue 3, July 2021, Page 251-257 PDF (570.09 K) | ||||
| Document Type: Original Article | ||||
| DOI: 10.21608/ajdsm.2021.66705.1183 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
Shaimaa Ibrahim Abdulrahman  1; Maged Mohammed Zohdy2
| ||||
| 1Fixed prosthodontics, faculty of dentistry, British University in Egypt, Cairo, Egypt | ||||
| 2Fixed prosthodontics, Faculty of dentistry, Ain Shams University, Cairo, Egypt | ||||
| Abstract | ||||
| Aim: The aim of this study was evaluating the effect of immediate and delayed dentin sealing on tensile bond strength of hybrid ceramic restorations Materials and methods: 60 extracted human molars were used. The occlusal surfaces were ground flat to expose the dentin surface using a low speed diamond saw. The prepared teeth were randomly divided into two groups according to the dentin sealing protocol. For group (D): Delayed Dentin Sealing was used and for group (I): Immediate Dentin Sealing was used. 60 vita enamic discs were machined into standard thickness of 2mm. For delayed dentine sealing samples, it was covered by a layer of temporary filling material directly after cutting. The provisional restoration was then removed after 48 hours and dentin was cleaned using airborne-particle abrasion (CoJet). For immediate dentine sealing samples, the single bond universal adhesive was applied and light cured immediately after cutting, and the provisionalization phase was done in the same manner of DDS group. The vita enamic discs were then cemented in its place for each group. The specimens in each group were then thermo-cycled, and tensile bond strength was measured using a Universal Testing Machine. One-way ANOVA was used to study the effect of different tested variables Results: Samples with IDS protocol showed higher tensile bond strength with vita enamic discs than DDS protocol. Conclusions: Immediate dentin sealing treatment would be recommended in high tensile stresses as it positively affect the bond strength of indirect restorations Keywords: Hybrid ceramics, Dentin Sealing, Tensile bond strength | ||||
| Keywords | ||||
| Hybrid ceramics; Dentin Sealing; Tensile bond strength | ||||
|