Inhibition of Mild Steel Corrosion in Sulfuric Acid Solution Using Extraction of Linum Usitatissimum Seeds
Elgahawi, H., Gobara, M., Baraka, A., Elthalabawy, W. (2017). Inhibition of Mild Steel Corrosion in Sulfuric Acid Solution Using Extraction of Linum Usitatissimum Seeds. EKB Journal Management System, 17(AEROSPACE SCIENCES & AVIATION TECHNOLOGY, ASAT - 17 – April 11 - 13, 2017), 1-17. doi: 10.21608/asat.2017.22454
Hassan Elgahawi; Mohamed Gobara; Ahmad Baraka; Waleed Elthalabawy. "Inhibition of Mild Steel Corrosion in Sulfuric Acid Solution Using Extraction of Linum Usitatissimum Seeds". EKB Journal Management System, 17, AEROSPACE SCIENCES & AVIATION TECHNOLOGY, ASAT - 17 – April 11 - 13, 2017, 2017, 1-17. doi: 10.21608/asat.2017.22454
Elgahawi, H., Gobara, M., Baraka, A., Elthalabawy, W. (2017). 'Inhibition of Mild Steel Corrosion in Sulfuric Acid Solution Using Extraction of Linum Usitatissimum Seeds', EKB Journal Management System, 17(AEROSPACE SCIENCES & AVIATION TECHNOLOGY, ASAT - 17 – April 11 - 13, 2017), pp. 1-17. doi: 10.21608/asat.2017.22454
Elgahawi, H., Gobara, M., Baraka, A., Elthalabawy, W. Inhibition of Mild Steel Corrosion in Sulfuric Acid Solution Using Extraction of Linum Usitatissimum Seeds. EKB Journal Management System, 2017; 17(AEROSPACE SCIENCES & AVIATION TECHNOLOGY, ASAT - 17 – April 11 - 13, 2017): 1-17. doi: 10.21608/asat.2017.22454

Inhibition of Mild Steel Corrosion in Sulfuric Acid Solution Using Extraction of Linum Usitatissimum Seeds

International Conference on Aerospace Sciences and Aviation Technology
Article 28, Volume 17, AEROSPACE SCIENCES & AVIATION TECHNOLOGY, ASAT - 17 – April 11 - 13, 2017, April 2017, Page 1-17  XML PDF (1.95 MB)
Document Type: Original Article
DOI: 10.21608/asat.2017.22454
View on SCiNiTO View on SCiNiTO
Authors
Hassan Elgahawi1; Mohamed Gobara2; Ahmad Baraka2; Waleed Elthalabawy2
1Libyan Armed Forces, Libya.
2Egyptian Armed Forces, Egypt.
Abstract
Inhibitive effect of Linum Usitatissimum (LU) on the acid corrosion of mild steel in 1M H2SO4 solution was studied by weight loss, Potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). Linum Usitatissimum effectively inhibited the corrosion of mild steel with efficiency ranges from 85.7 to 95.5 % for LU concentrations from 80 to 1200 ppm. EIS showed that the charge transfer governs the corrosion process of mild steel in 1M H2SO4 solution. Adsorption isotherm study was performed using weight loss measurements where Langmuir and El-Awady models were applied on data to investigate the model of adsorption. Corrosion inhibition was also tested at different temperatures to measure the thermodynamic parameters; ΔG°, ΔH°, ΔS° and Ea. Inhibition was suggested to occur due to adsorption phenomenon and data obey the Langmiur model. Thermodynamic study reveals that adsorption is exothermic–physical process driven by entropic factors. The morphology study using SEM confirms the electrochemical investigation where the corrosion resistance increases with increase of inhibitor concentration.
Keywords
Corrosion; Linum Usitatissimum; mild steel; EIS; SEM