Synthesis, characterization of titania supported on mesoporous MCM-41 and its application for the removal of methylene blue | ||||
| Delta University Scientific Journal | ||||
| Volume 5, Issue 2, September 2022, Page 321-339 PDF (1.02 MB) | ||||
| Document Type: Original research papers | ||||
| DOI: 10.21608/dusj.2022.275549 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
Reda Salama ; Sohier Abd Elhakim* ; Salem Samra* ; Shady El-Dafrawy* ; Amr Awad Ibrahim* ; Awad Ahmed 
| ||||
| Abstract | ||||
| Solid acid substance of MCM-41 prepared by sol-gel method followed by incorporation of TiO2 within the mesochannels through a simple and effective impregnation method. TiO2 loaded on MCM-41 were synthesized at room temperature using tetraethoxysillane (TEOS), Cetyltrimethylammonium bromide (CTAB) as template and titanium (IV) isopropoxide (TIP) as titanium source. The resultant mesoporous TiO2/MCM-41 samples were calcined at 550 0C. The resultant samples were characterized using X-ray diffraction patterns (XRD), BET measurements, FT-IR and high-resolution transmission electron microscopy (TEM). Nitrogen adsorption-desorption measurements were used to measure surface area and average pores diameter at -1960C. The TiO2/MCM-41 with higher Ti/Si ratio shows low structural integrity and the formation of Ti-oxide species leading to a considerable decrease in surface area. The activities of TiO2/MCM-41 for adsorption of methylene blue (MB) studied in details. Adsorption increase with the modification of MCM-41 by TiO2 up to 25% of TiO2 then decreased. The samples of 25% TiO2 loaded on MCM-41 show higher catalytic activity. | ||||
| Keywords | ||||
| TiO2 loaded MCM-41; sol-gel; TEOS; water treatment; Methylene Blue | ||||
|