Structural and magnetic properties of chromium substituted lithium zinc ferrite nanoparticles | ||||
| Bulletin of Faculty of Science, Zagazig University | ||||
| Article 3, Volume 2023, Issue 1, March 2023, Page 24-31 PDF (493.07 K) | ||||
| Document Type: Original Article | ||||
| DOI: 10.21608/bfszu.2022.157337.1172 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
N. Abu-Elsaad  1; S. Mazen2; A. Sleem2
| ||||
| 1physics department, faculty of science, Zagazig University, Zagazig, Egypt. | ||||
| 2Physics Department, Faculty of Science, Zagazig University, Zagazig, Egypt | ||||
| Abstract | ||||
| The structural and magnetic characteristics of Li0.4Zn0.2CrxFe2.4-xO4 (x = 0.0, 0.1, 0.2, 0.3, 0.4 and 0.5) ferrites produced via citrate auto-combustion were investigated. Various intriguing modifications in the values of structural factors such as lattice constant, crystallite size, and X-ray density have been detected as the Cr3+ concentration is raised. X-ray diffraction validated the cubic spinel structure's single phase. The lattice parameter drops as the chromium concentration rises. The wide lines suggest that the particles are nano-sized, and the crystallite size (t) was determined to be between 23 and 27 nm. The estimated crystallite size from Williamson–Hall formula decreased with Cr concentration until x=0.4 and then rises at x=0.5. After annealing the samples at 1000 oC, several magnetic characteristics were tested at ambient temperature. The magnetization M was recorded in the magnetic field up to 5500 Am-1. In addition, the influence of the applied magnetic field on relative permeability (μr) was discussed. | ||||
| Keywords | ||||
| Li-Zn-Cr ferrite; XRD; Magnetic properties | ||||
|