Shear Bond Strength of Pulp Capping Materials to Dentin After One Day: MTA versus Bio-Dentin | ||
| Egyptian Dental Journal | ||
| Article 2, Volume 69, Issue 2 - Serial Number 5, April 2023, Pages 1555-1559 PDF (448.17 K) | ||
| Document Type: Original Article | ||
| DOI: 10.21608/edj.2023.180041.2372 | ||
| Authors | ||
| Ashraf Amin* 1; Mona Hafez2 | ||
| 1Associate Professor, Endodontics Department, Faculty of Dentistry, Karf Elsheikh University | ||
| 2Associate Professor, Conservative Department, Faculty of Dentistry, Karf Elsheikh University | ||
| Abstract | ||
| Aim of the study: evaluate and compare shear bond strength of MTA and Bio-Dentin to dentin after one day. Materials and Methods: Thirty upper premolars were selected and sectioned1 mm above the level of pulp horns to expose much dentin, specimens were randomly assigned into three groups, n=10 each. MTA, Bio-Dentin and calcium hydroxide (control) were mixed then filled in tubes [diameter & height = 3mm] then applied on dentin surfaces. After one day, the shear bond strength was tested using a universal testing device. A Stereo microscope was used to assess failure modes. Results: After one day, setting of these capping materials, shear bond strength of MTA and Bio-Dentin were significantly different from that of calcium hydroxide. However, shear bond strength of MTA and Bio-Dentin were not significantly different. Calcium hydroxide showed 100% adhesive failure, Bio-Dentin showed 12% mixed failure while MTA showed 15% mixed failure. Conclusion: After one day setting, MTA and Bio-Dentin showed shear bond strength higher than that of Calcium Hydroxide with some precedence to Bio-Dentin. Keywords: MTA, Bio-Dentin, Shear Bond Strength, Pulp Capping Materials. | ||
| Keywords | ||
| MTA; Bio-Dentin; Shear Bond Strength; Pulp Capping Materials | ||
|