Evaluation Of The Physical Properties Of Sealapex Incorporated With Calcium HydroxideNanoparticles (An In-Vitro Study) | ||||
Journal of Fundamental and Clinical Research | ||||
Article 8, Volume 3, Issue 2, December 2023, Page 139-153 PDF (568.52 K) | ||||
Document Type: Original research articles | ||||
DOI: 10.21608/jfcr.2023.248576.1063 | ||||
![]() | ||||
Authors | ||||
Rana Alaa-eldin Shafei1; Abeer Hashem Mahran![]() ![]() | ||||
1Endodontic Department. Faculty of Oral and Dental Medicine. Misr International University, cairo, egypt | ||||
2Endodontic Department. Faculty of Dentistry. Ain Shams University, Cairo, Egypt. | ||||
3Endodontic department, Faculty of oral and dental medicine, Misr International University | ||||
Abstract | ||||
Background: Nanotechnology is used in enhancing some existing materials.Nano-calcium hydroxide sealers are introduced to eliminate the short-comings of the conventional one. Objectives: To evaluate the physical properties of Sealapex incorporated with calcium hydroxide nanoparticles(CHNP). Methods:Calcium hydroxide nanoparticles were incorporated to Sealapex root canal sealer in concentrations of 3% and 8% by weight respectively.Three groups were established: Group I (Sealapex+3%CHNP), Group II (Sealapex+8%CHNP) and Group III (Sealapex in the conventional formula).Solubilitywasevaluatedaccording to ISO standardization 6878:2012 specificationand evaluated at time intervals of (24 hours and 14 days). ForpH assessment, specimens were immersed in deionized water and measured using a pH meter at time intervals of (1, 3, 24 hours and 14 days).Results:Group II (Sealapex+8%CHNP) showed a significantly lowersolubility value at 24 hours and the highest pH value after 3 hours. Conclusions:The addition of 3% CHNP to Sealapex resulted in a negative effect on the solubility of the sealer but enhanced its alkalinity.On other hand, the addition of 8% CHNP enhanced the physical properties of the sealer.Clinical Significance: The addition of nanoparticles to currently existing sealer formulas may enhance its physical properties and eliminate some of its drawbacks. | ||||
Keywords | ||||
Calcium hydroxide; Endodontic sealers; Nano-calcium hydroxide; Sealapex | ||||