IMPACT OF INTEGRATING CRACK BRIDGING PHENOMENON ON THE FRACTURE RESISTANCE AND FRACTURE MODE OF THREE DIFFERENT ENDOCROWN RESTORATIONS IN ENDODONTICALLY TREATED POSTERIOR TEETH AN IN-VITRO STUDY | ||||
| Egyptian Dental Journal | ||||
| Volume 71, Issue 2 - Serial Number 5, April 2025, Page 1911-1924 PDF (1.15 MB) | ||||
| Document Type: Original Article | ||||
| DOI: 10.21608/edj.2025.364788.3405 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
Dalia Ali Moukarab   1; shams waz 2; Safaa helmy Abd-Elhakim 3
| ||||
| 1Associate professor, Endodontics, Faculty of Dentistry, Minia University, Minia, Egypt | ||||
| 2Associate professor, Fixed Prosthodontics, Faculty of Dentistry, Minia University, Minia, Egypt. | ||||
| 3lecturer, Conservative Dentistry, Faculty of dentistry, Minia university, Minia, Egypt | ||||
| Abstract | ||||
| Aim of study: Compare three endocrown restorations using crack bridging material beneath them on the fracture resistance and fracture mode in endodontically treated posterior teeth. Material and methods: Fifty mature mandibular molars were selected. The samples were divided to five equal groups(n=10). Group (CN) 10 samples were kept untreated, Group (CP) 10 samples were endodontically treated only, the three test groups were subjected to root canal treatment and a standard butt joint endocrown preparation was done followed by application of 2mm Ever-X flow flowable composite to cover the floor of the pulp chamber. Group (EEC) 10 samples restored with Ever- X posterior composite endocrown, Group (EIM) 10 samples restored with IPS E-max CAD endocrown and Group (ECS) 10 samples restored with Cerasmart CAD/CAM endocrown. Following thermocycling fracture resistance and mode were assessed. Results: The experimental groups (EEC, EIM, and ECS) showed comparable fracture resistance values of 1085.3±99.5, 1126.3±92.9, and 1111.4±90.8 respectively. There were no significant differences between the experimental groups (EEC vs EIM p=0.376, EEC vs ECS p=0.571, EIM vs ECS p=0.747), suggesting similar performance among these treatments. Type III fractures were most prevalent in all groups. Type IV fractures were less common, with EIM showing the highest occurrence (20%). While there are some variations in fracture modes between groups, these differences are not statistically significant. Conclusion: Placing short fiber reinforced composite base beneath endocrown restorations not only produced near to intact tooth fracture resistance values but also yielded favorable modes of fracture. | ||||
| Keywords | ||||
| Crack bridging; Endocrown; Short fiber reinforced composite; Fracture resistance; Fracture mode | ||||
|