IN VITRO EVALUATION OF MICROLEAKAGE AND SHEAR BOND STRENGTH OF SELF-ADHESIVE HYBRID COMPOSITES IN PRIMARY MOLARS | ||||
| Alexandria Dental Journal | ||||
| Article 2, Volume 50, Issue 2, August 2025, Page 226-234 PDF (571.97 K) | ||||
| Document Type: Original Article | ||||
| DOI: 10.21608/adjalexu.2025.326823.1543 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
Mahmoud Magdy Mohamed  1; azza hanno1; Sally Mohamed Abdelkader2; sara Ibrahim Mohamed Zeitoun3
| ||||
| 1pediatric dentistry and dental public health department, faculty of dentistry, alexandria university, alexandria, egypt | ||||
| 2Dental Material Department ,Faculty of Dentistry-Alexandria University, Alexandria, Egypt | ||||
| 3Lecturer of Pediatric Dentistry and Dental Public Health Department of Pediatric Dentistry and Dental Public Health Faculty of Dentistry -Alexandria University | ||||
| Abstract | ||||
| Introduction: Recently the self-adhesive hybrid composite, Surefil One™ was introduced as a “bioactive material”. Objectives: To assess microleakage and shear bond strength of Surefil One™ in comparison to Cention forte and resin-based composite used as restorations in primary molars. Methodology: 66 sound primary molars were randomly divided into two main groups (groups A and B). Each group was subdivided randomly into three equal subgroups. Groups (IA, IIA, and IIIA): were assigned to the microleakage evaluation test. A standardized box was prepared and restored with Surefil One™ (IA), Cention Forte (IIA) and Spectra™ ST HV (IIIA). Teeth were thermocycled, immersed into methylene blue solution for 24 hours, sectioned longitudinally, and examined under a stereomicroscope. Groups (IB, IIB, and IIIB): were assigned for the shear bond strength test. Surefil One™ (IB), Cention Forte (IIB) and Spectra™ ST HV (IIIB) were applied on the grounded buccal surface. A universal testing machine was used to assess the shear bond strength, and a stereomicroscope was used to evaluate mode of failure in each specimen. Kruskal Wallis test, One Way ANOVA were used to compare microleakage, shear bond strength respectively. Results: Penetration percentage was recorded in the Cention forte specimens (22.87%), followed by Spectra™ ST HV (50.00%), whereas Surefil One scored (65.71%) p < 0.0001. Cention forte samples showed shear bond strength (9.89 ±3.24 MPa), followed by Surefil One (4.57 ±1.98 MPa), then Spectra™ ST HV (4.47 ±2.20 MPa) p < 0.0001. Conclusion: Cention forte demonstrated less leakage and more retention than Spectra™ ST HV and Surefil One. | ||||