Effect of Aging on Marginal Adaptation and Fracture Resistance of Differently Designed CAD/CAM Restorations for Endodontically Treated Single Rooted Teeth | ||||
| Al-Azhar Journal of Dentistry | ||||
| Volume 2023, Issue 1, January 2023 | ||||
| DOI: 10.58675/2974-4164.1581 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
| Sara A. Eldin1; Jylan Elguindy2; Atef F. Ahmed3; Shereen K. Salem1 | ||||
| 1Fixed Prosthodontics, Faculty of Dentistry, October 6 University, Giza | ||||
| 2Fixed Prosthodontics, Faculty of Oral and Dental Medicine, Cairo University, Cairo | ||||
| 3Crown and Bridges Department, Faculty of Dental Medicine for Girls, Al-Azhar University | ||||
| Abstract | ||||
| Purpose: To evaluate the effect of aging on marginal adaptation and fracture resistance of two CAD/CAM designs and ceramic materials to restore endodontically treated premolars. Materials and Methods: Forty extracted upper second premolars were collected (single rooted, single canal), cleaned and endodontically treated, then divided into 2 main groups (n=20) each having a different restoration design. Group I (fiber-post, composite core, and crown), Group II (endocrowns). Preparations were done according to each restoration design guidance. Each group was divided into 2 subgroups (n=10) according to the used material; Vita Enamic (E), Vita Suprinity(S); Subgroups IE, IIE and IS, IIS respectively. Prepared teeth were scanned, different restoration designs were milled, finished, then cemented on their respective preparations. Samples of each subgroup were divided into 2 divisions (n=5). Division (A): Aged and division (N): Non-aged. Marginal adaptation records were measured taken before and after aging for both divisions followed by fracture resistance test. Results: Aging had no significant effect on marginal gap of all samples irrelevant of the material & design. Subgroup (E) showed significantly lower marginal adaptation compared to subgroup (S). On the other hand, aging significantly decreased fracture resistance of both groups; group (I) recorded significantly higher fracture resistance than group 2. There were insignificant fracture resistance results among tested divisions. Conclusion: Aging has no drastic effect on marginal adaptation of both groups. Irrelevant of the material used, however, fracture resistance was decreased for both groups and sup groups after aging. | ||||
| Keywords | ||||
| : Marginal adaptation; Fracture resistance; Endocrown; Vita Enamic; suprinity | ||||
|