Synthesis and Characterization of Photocurable Resin Used in 3D Printing for Dental Applications | ||||
| Al-Azhar Journal of Dentistry | ||||
| Volume 2023, Issue 1, January 2023 | ||||
| DOI: 10.58675/2974-4164.1568 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
| Mayar E. Mohamed1; Inas T. Motawea2; Hisham Essawy3 | ||||
| 1Post graduate student Department of Dental Biomaterials, Faculty of Dental Medicine for Girls, Al-Azhar University, Cairo, Egypt. | ||||
| 2Professor of Dental Biomaterials, Dean of Faculty of Dental Medicine for Girls Al-Azhar University, Cairo, Egypt | ||||
| 3Professor at polymer chemistry and pigments Department, National Research center, Cairo, Egypt | ||||
| Abstract | ||||
| Purpose: The present study aimed to synthesize and characterize photocurable resin with lower cost to be used in DLP 3D printing to fabricate clear dental appliances like surgical guides and aligners. Materials and Methods: Mixture of acrylates of 1,10 decandiol diacrylate, pentaerythritol tetracrylate and isobornyl acrylare were mixed together and dissolve the photo initiator phenyl bis (2,4,6 trimethylbenzoyl) phosphine oxide and optical absorber 2,5-bis (tert-butyl-benzoxzzol-2-yl) thiophene by proper mixing for 30 mins at room temperature. Then experimental resin specimens were fabricated by DLP 3D printer 12 specimens were subjected to post curing for 15 mins and another 12 specimens were subjected to 25 mins post curing. Characterization was demonstrated by scanning electron microscope (SEM), thermo gravimetric analysis, and Fourier transform infrared (FTIR). Flexural strength was examined by three-point loading under universal testing machine, translucency was examined by spectrophotometer, and degree of convergence was calculated gravimetrically. Results: Results revealed successful fabrication of photocurable resin. The resin showed excellent surface finish under scanning electron microscope, thermally stable up to 500 °C. FTIR confirmed functional group matching with the target copolymer. Regarding flexural strength results, it was found that no significant difference between two groups (p ≥ 0.05) however translucency results revealed significant difference between two groups (p ≤ 0.05). Conclusion: Possible fabrication of photocurable resin to be used in DLP 3D printer. | ||||
| Keywords | ||||
| additive manufacturing; 3D printing; photocurable resins | ||||
|