Comparative Evaluation of Chitosan and Nano-chitosan Final Irrigant Solution on The Push Out Bond Strength of Bio-ceramic Sealer | ||||
| Al-Azhar Journal of Dentistry | ||||
| Volume 2023, Issue 1, January 2023 | ||||
| DOI: 10.58675/2974-4164.1590 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
Khadija Salem1; Mohsen Nour-Eldin2; Fatma. A Taher3; Heba Abdelkafy 4
| ||||
| 1Dentist at Ministry of Health, Libya | ||||
| 2Professor of Endodontics, Department of Endodontic, Faculty of Dental Medicine for Girls, Al-Azhar University, Cairo ,Egypt | ||||
| 3Chemistry Department, Faculty of Science, Al-Azhar University (Girls), Nasr City Cairo, Egypt. | ||||
| 4Lecturer of Endodontics, Department of Endodontic, Faculty of Dental Medicine for Girls, Al-Azhar University, Cairo ,Egypt | ||||
| Abstract | ||||
| Purpose: EndoSeal MTA sealer push-out bond strength was evaluated after using Chitosan and Nano-Chitosan as the final rinse. Materials & methods: Universal ProTaper rotary device was utilized to instrument 28 natural human single rooted lower bicuspid teeth, followed by one minute irrigation by 2.6% sodium hypochlorite. All samples were classified randomly into four main groups [n=7] as per the utilized final rinse; Group S: Normal saline, Group E: 17%EDTA, Group CH: 0.2% Chitosan, Group CNP: 0.2%Nano-Chitosan. The final rinse was standardized to be 5ml/ 3min for each solution. Obturation of all samples was carried out with ProTaper GP and EndoSeal MTA sealer, then placed in a humidifier for 1week. All roots were sectioned into horizontal slices of 2 mm thickness and immersed in self-curing acrylic resin. The samples were put through a push-out test with a 0.5mm/min loading speed. Data was statistically analyzed. Results: The chitosan at the coronal level (Group CH) showed the greatest push-out bond strength, followed by groups CNP, EDTA and S with statically significant difference (P value< 0.05) among all tested groups versus the control one. While at the apical level the highest push out bond strength was observed in EDTA group followed by groups CH, CNP and S with statically significant difference between all the tested groups versus the control one. Conclusion: Chitosan and its Nano counterpart have a comparable result to EDTA irrigant solution. Different chelating agents can greatly influence EndoSeal sealer push-out bond strength. | ||||
| Keywords | ||||
| Endoseal MTA; Nano-chitosan; Push-out | ||||
|