SURFACE INVESTIGATIONS OF ALUMINUM IN 2M HYDROCHLORIC ACID SOLUTION IN THE PRESENCE OF POTASSIUM IODATE INHIBITOR
EL MAGHRABY, A. (2630). SURFACE INVESTIGATIONS OF ALUMINUM IN 2M HYDROCHLORIC ACID SOLUTION IN THE PRESENCE OF POTASSIUM IODATE INHIBITOR. EKB Journal Management System, 2009(6), 43-49. doi: 10.21608/absb.2009.7542
A. EL MAGHRABY. "SURFACE INVESTIGATIONS OF ALUMINUM IN 2M HYDROCHLORIC ACID SOLUTION IN THE PRESENCE OF POTASSIUM IODATE INHIBITOR". EKB Journal Management System, 2009, 6, 2630, 43-49. doi: 10.21608/absb.2009.7542
EL MAGHRABY, A. (2630). 'SURFACE INVESTIGATIONS OF ALUMINUM IN 2M HYDROCHLORIC ACID SOLUTION IN THE PRESENCE OF POTASSIUM IODATE INHIBITOR', EKB Journal Management System, 2009(6), pp. 43-49. doi: 10.21608/absb.2009.7542
EL MAGHRABY, A. SURFACE INVESTIGATIONS OF ALUMINUM IN 2M HYDROCHLORIC ACID SOLUTION IN THE PRESENCE OF POTASSIUM IODATE INHIBITOR. EKB Journal Management System, 2630; 2009(6): 43-49. doi: 10.21608/absb.2009.7542

SURFACE INVESTIGATIONS OF ALUMINUM IN 2M HYDROCHLORIC ACID SOLUTION IN THE PRESENCE OF POTASSIUM IODATE INHIBITOR

Al-Azhar Bulletin of Science
Volume 2009, Issue 6, June 2009, Pages 43-49
DOI: 10.21608/absb.2009.7542
Author
A. EL MAGHRABY
Chemistry department, Faculty of science, Cairo University, Giza, Egypt,
Abstract
The results of investigations by using optical, scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS) to study the surface morphology, the composition of adsorbed film formed on the surface of aluminum samples in 2M hydrochloric acid solution containing ppm optimum KIO3 dose. The data reveal that the additive improves the surface morphology of aluminum, due to the marked layer enrichment of Al- surface by inhibitor components. Detailed studies were carried out to investigate the effect of oxygen in the inhibition process. The nature and strength of the passive film and the mechanism of its formation are explained based on detailed studies conducted under experimental conditions.