Effect of different surface treatments and time of repair on shear bond strength of fiber reinforced resin composite material. | ||
| Ain Shams Dental Journal | ||
| Volume 37, Issue 1, March 2025, Pages 511-520 PDF (1.25 M) | ||
| Document Type: Original articles | ||
| DOI: 10.21608/asdj.2024.320563.1511 | ||
| Authors | ||
| Aisha Magdy Abd El Aziz* 1; Eman Nasser Ahmed Diab2; Omaima Hassan Ghallab3 | ||
| 1Department of Operative Dentistry, Faculty of Dentistry, Ain Shams University, Cairo, Egypt | ||
| 2Department of Operative dentistry,Faculty of Dentistry, Ain Shams University, Cairo,Egypt | ||
| 3Restorative Department, Faculty of Dentistry, Ain Shams University | ||
| Abstract | ||
| Aim: This study evaluates how repair time and surface treatments affect the shear bond strength between fiber-reinforced resin composite and giomer material. Materials and methods: A total of 100 disc samples (2x5mm) of fiber-reinforced composite resin (everX Posterior, GC Corporation, Tokyo, Japan) were prepared and divided into groups based on repair time (immediate and delayed) and surface treatments (five subgroups: subgroup (1): No surface treatment (negative control), subgroup (2): Diamond bur, phosphoric acid etch, universal adhesive, subgroup (3): Diamond bur, phosphoric acid etch, universal adhesive, silane, subgroup (4): Air abrasion, phosphoric acid etch, universal adhesive, (5): Air abrasion, phosphoric acid etch, universal adhesive, silane). A bulk-fill giomer material (Beautifil-Bulk Restorative, Shofu, Kyoto, Japan) was used as a material of repair in 4 mm thickness. After that, samples underwent 5000 cycles of thermocycling and were subjected to shear bond testing using a Universal Testing Machine. Data were analyzed using one-way ANOVA and Tukey post-hoc tests (p≤0.05). Results: Surface treatments have shown statistically significant effect on shear bond strength of repaired fiber-reinforced resin composite at immediate repair where air abrasion groups showed highest SBS while negative control group showed lowest SBS. Different surface treatments have shown non-significant difference at delayed repair groups. Time of repair has shown statistically significant effect on most groups where SBS increased significantly at delayed repair except for A+P+U and A+P+U+Si groups. Conclusion: Time lapse significantly affects repaired fiber reinforced composite durability, while surface treatment and silane having minimal impact. | ||
| Keywords | ||
| Fiber-reinforced composite resin; repair; surface treatments; giomer; shear bond strength | ||
|