Preparation and characterization of silver nanoparticles homogenous thin films | ||
| NRIAG Journal of Astronomy and Geophysics | ||
| Volume 7, Issue 1, June 2018, Pages 27-30 PDF (1.45 M) | ||
| DOI: 10.1016/j.nrjag.2018.04.002 | ||
| Authors | ||
| Maroof A. Hegazy; E. Borham | ||
| Abstract | ||
| The wet chemical method by metal salt reduction has been widely used to synthesize nanoparticles. Accordingly the silver nitrate used as silver precursor and sodium borohydrate as reduction agent. The silver nanoparticles were characterized by different characterization techniques including UV–VIS spectrometry, Transmission electron microscope (TEM), and Zeta potential technique. Thin films of the colloidal solution were fabricated using direct precipitation technique on ITO glass, silicon substrate and commercial glass substrate and characterized by imaging technique. The absorption peak of the silver nanoparticles colloidal solution was around 400 nm. The TEM images indicate that the silver nanoparticles had spherical shape and their sizes were from 10 to 17 nm. The particle size of the silver nanoparticles was confirmed by Zeta potential technique. The imaging technique indicated that the homogeneous distribution of the colloidal silver solution thin film on the silicon substrate was stronger than the ITO glass and inhomogeneous film was emerged on the commercial glass. | ||
| Keywords | ||
| nano-silver; TEM; UV; Zeta potential; Thin film | ||
|
Statistics Article View: 8 PDF Download: 14 |
||