Microwave synthesis of Lithium aluminum silicate and its characterization | ||||
| The International Conference on Electrical Engineering | ||||
| Article 57, Volume 1, 1st International Conference on Electrical Engineering ICEENG 1998, March 1998, Page 582-591 PDF (1.54 MB) | ||||
| Document Type: Original Article | ||||
| DOI: 10.21608/iceeng.1998.62255 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
| M. SH. Fayed; SH. R. Gooda; W. F.F. Mekky | ||||
| Armed Forces of Egypt. | ||||
| Abstract | ||||
| Lithium aluminum silicate (LAS) was prepared using :he sol-gel technique and starting from LiCI H2O, Al(NO3)3 and Tetraethyl ortho silicate (TEOS). The final product Li20 : A1203 : 3SiO2. Ac id catalysis was applied by using of HNO3, 113PO4 or HC1O4 in addition 1.) a catalyst free sample. Microwave heatitg was employed in both the hydrolysis, condemiation and drying processes. The prepared samples were thermally analyzed by thermogravemetric analysis (TGA) and scanning electron microscope (SEM). TGA thermograms showed sharp decrease in weight at 250°c that varied with the catalyst. SEM analysis also indicated variable shapes of the crystals with different catalysts. | ||||
|
Statistics Article View: 147 PDF Download: 211 |
||||