THE RELATION BETWEEN THE MICROSTRUCTURE OF CARBON STEEL (0.24 C% & 0.38 C%) AND CORROSION PROTECTION
Ali, A., SELIM, S., MOHAMED, A., Al-Hazmi, G., Ali, A. (2008). THE RELATION BETWEEN THE MICROSTRUCTURE OF CARBON STEEL (0.24 C% & 0.38 C%) AND CORROSION PROTECTION. EKB Journal Management System, 2008(6), 179-194. doi: 10.21608/absb.2008.9002
A. Ali; S. R. SELIM; A. A. MOHAMED; G. A. Al-Hazmi; A. H. Ali. "THE RELATION BETWEEN THE MICROSTRUCTURE OF CARBON STEEL (0.24 C% & 0.38 C%) AND CORROSION PROTECTION". EKB Journal Management System, 2008, 6, 2008, 179-194. doi: 10.21608/absb.2008.9002
Ali, A., SELIM, S., MOHAMED, A., Al-Hazmi, G., Ali, A. (2008). 'THE RELATION BETWEEN THE MICROSTRUCTURE OF CARBON STEEL (0.24 C% & 0.38 C%) AND CORROSION PROTECTION', EKB Journal Management System, 2008(6), pp. 179-194. doi: 10.21608/absb.2008.9002
Ali, A., SELIM, S., MOHAMED, A., Al-Hazmi, G., Ali, A. THE RELATION BETWEEN THE MICROSTRUCTURE OF CARBON STEEL (0.24 C% & 0.38 C%) AND CORROSION PROTECTION. EKB Journal Management System, 2008; 2008(6): 179-194. doi: 10.21608/absb.2008.9002

THE RELATION BETWEEN THE MICROSTRUCTURE OF CARBON STEEL (0.24 C% & 0.38 C%) AND CORROSION PROTECTION

Al-Azhar Bulletin of Science
Article 12, Volume 2008, Issue 6, June 2008, Page 179-194  XML PDF (658.8 K)
Document Type: Original Article
DOI: 10.21608/absb.2008.9002
View on SCiNiTO View on SCiNiTO
Authors
A. Ali1; S. R. SELIM* 2, 3; A. A. MOHAMED4; G. A. Al-Hazmi1; A. H. Ali1
1Chemistry Department, Faculty of Science, Taiz University, Taiz, YEMEN
2Chemistry Department, Faculty of Science, Al-Azhar University, Cairo, EGYPT
3Chemistry Department, Faculty of science, Taiz University, Taiz, YEMEN.
4Chemistry Department, Faculty of Science, Al-Azhar University, Cairo, EGYPT.
Abstract
The effect of carbon percent on the corrosion of steel in ethanol – aqueous H2SO4 solution has been studied by using weight loss technique. The effect of presence of foreign atoms in steel composition on the corrosion resistance has been investigated. Beside that, the effect of heat treatment on the corrosion rates has been interpreted. The inhibitive action of N, N-dihydroxy ethyl acryl-amide on the corrosion rate of steel appears high efficiency for all samples in all cases under study. The corrosion behavior is interpreted in view of the microstructure of samples before and after heat treatment. There are two wet corrosion processes that affected by carbon percent in the localized area. Before heat treatment the corrosion rate is more dependent upon inter-granular corrosion type while, increasing C % or by quenching regime the corrosion rate is more dependent upon allotropic–galvanic corrosion type. The corrosion rate in absence of inhibitors classified as cathodic control while it classified as cathodic–anodic control in presence of inhibitor.
Keywords
steel microstructure; corrosion of low and medium carbon steel; N, N-dihydroxy ethyl acryl-amide; Heat treatment