Some Properties of Compressed Rice Straw | ||||
| Annals of Agricultural Science, Moshtohor | ||||
| Article 1, Volume 53, Issue 4, 2015, Page 539-548 PDF (744.35 K) | ||||
| Document Type: Original Article | ||||
| DOI: 10.21608/assjm.2015.109933 | ||||
 View on SCiNiTO | ||||
| Abstract | ||||
| Rice straw was investigated as a raw material for manufacturing a composite for using as a building material. Commercial urea formaldehyde "UF" adhesive was used as a binder in manufacturing process. Different formation pressures "FP" of (5.7, 12.4 and 18.5 MPa) and different percentages of urea formaldehyde "UF" of (20-40 %) were used in the manufacturing products. Some properties of water absorption percentage "WA" (%), thickness swelling "TS" (mm) and Acoustic insulation percentage "AI" (%) were measured and analyzed for the produced composite. The properties of the produced composite were dependent on formation pressures "FP" (MPa) and binding materials percentages "UF" (%). The results show that the lowest values of "WA" and "TS" were 110.6 (%) and 4.85 (mm) at "FP" of 18.51 (MPa) and "UF" of 4o (%) after immersion time of 5 min., respectively while the highest value of "AI” was 9.66 (%) at "FP" of 5.68 (MPa) and "UF" of 20 (%). Three prediction equations were developed for the previous properties respectively. | ||||
| Keywords | ||||
| Rice straw; adhesive; composite; properties; compressed | ||||
|
Statistics Article View: 97 PDF Download: 147 |
||||