Development and Crystallization Study of Li2O-B2O3-SiO2 Glass Ceramic Rich with ZrO2 | ||||
Egyptian Journal of Chemistry | ||||
Article 6, Volume 54, Issue 1, February 2012, Page 81-97 PDF (823.28 K) | ||||
DOI: 10.21608/ejchem.2011.1381 | ||||
View on SCiNiTO | ||||
Abstract | ||||
GLASS ceramic in the system Li2O-B2O3-SiO2 was prepared by adding different amounts of ZrO2 up to maximum saturation. DTA, XRD and SEM were used to study the crystallization behavior of these glass samples. Tetragonal and monoclinic zirconia, are the only crystallized phases obtained after different heat treatment schedules. Fraction of transformed ZrO2 and total intensity of ZrO2 were calculated. Microhardness was measured for different samples, and it was found to be depending on the amount of ZrO2 added and the heat treatment parameters. Sample contains 20 g ZrO2 and treated at 650ºC for 10 hr showed higher microhardness value (14.99GPa). | ||||
Keywords | ||||
hardness; Glass-ceramic; Borosilicate; Zirconia and Martensitic transformation | ||||
Statistics Article View: 286 PDF Download: 426 |
||||