ICMMS-2: Enhancement of The Dielectric and Nonlinear Optical Properties of PbSe Nanomaterial Thin Films with Different Contents of Polyethylene Glycol | ||||
Egyptian Journal of Chemistry | ||||
Article 1, Volume 64, Issue 3, March 2021, Page 1101-1107 PDF (637.09 K) | ||||
Document Type: Original Article | ||||
DOI: 10.21608/ejchem.2021.55832.3178 | ||||
View on SCiNiTO | ||||
Authors | ||||
Samia A. Gad1; Ahmed Abdel Moez2; Gehan M. Mahmoud2; Fatma S. Terra2 | ||||
1Semiconductor Laboratory, Solid State Physics Department, Physics Research Division, National Research Centre, 33 El-Bohouth Street, Dokki, Giza 12622, Egypt. | ||||
2Solid State Electronics Laboratory, Solid State Physics Department, Physics Research Division, National Research Centre, 33 El-Bohouth Street, Dokki, Giza 12622, Egypt. | ||||
Abstract | ||||
PbSe nanocrystals doped with poly ethyleneglycol (PEG) were prepared using hydrothermal method. The reflectance spectra (R) were measured for these samples, and also refractive index (n) values were calculated, which increase with PEG ratio. Both of (Ed) and (Eo) increase with PEG content, while (N/m*) ratio decreased with PEG content. While all of (M-1), (M-3) and static refractive index (no), were determined. (ε\) and (ε\\) peak position decrease with photon energy (hν). Also both of (σ1) and (σ2) decrease with (hν), while (χ(1)) increases with (hν) for all samples. The nonlinear optical parameters such as, (n2) and (χ(3)) decrease with PEG, as a result of increasing the sample density with PEG. (βc), were determined theoretically. Both electrical susceptibility (χ(e)) and relative permittivity (ε(r)) has blue shift with (hν) for all samples. (Nc/ m*e (cm-3)), (Nv/m*h (cm-3)) were calculated theoretically. | ||||
Keywords | ||||
PbSe nanocrystals with different PEG contents; optical conductivity; dielectric properties; nonlinear optical properties; semiconducting properties | ||||