Cure Characteristics and Physicomechanical Properties of Calcium Carbonate Reinforcement Rubber Composites | ||||
| Egyptian Journal of Solids | ||||
| Article 12, Volume 26, Issue 2, 2003, Page 241-257 PDF (1.16 MB) | ||||
| DOI: 10.21608/ejs.2003.150162 | ||||
 View on SCiNiTO | ||||
| Abstract | ||||
| Cure characteristics and physicomechanical properties of calcium carbonate, CaCO3, reinforced rubbers (NR, NBR) were studied. Minimum torque, maximumminimum torque, cure rate and the scorch and cure time of the prepared rubber compounds were assessed by using a Monsanto Oscillating Disc Rheometer (ODR- 100). Stress and strain at yield and at rupture before and after aging were determined by using a Zwick tensile testing machine (Model 1425). Results showed that cure time, cure rate index (CRI), maximum torque, stress and strain at yield demonstrated clearly the optimum filler content for each type of rubber. Values of the rubber-filler interaction parameter (m) were 0.585 and 0.175 for NR and NBR respectively and suggested good NR-filler interaction than that of NBR where the dilution effect of NBR becomes more significant as the filler loading is increased. The aging behavior (resistance to deterioration) of the prepared rubber compounds due to the prolonged exposure of γ-irradiation was estimated by plotting the percent-retained values of the physicomechanical properties at different γ-doses. | ||||
|
Statistics Article View: 84 PDF Download: 575 |
||||