Effect Of Flexural Strength Of Denture Base Resin Reinforced By Three Different Nanoparticle Materials (In Vitro Study) | ||||
Al-Azhar Assiut Dental Journal | ||||
Article 4, Volume 4, Issue 1, April 2021, Page 31-36 PDF (942.01 K) | ||||
Document Type: Original Article | ||||
DOI: 10.21608/aadj.2021.163878 | ||||
View on SCiNiTO | ||||
Authors | ||||
Mohamed Aboshama* 1; Noha Helmy2; Mahmoud Ammar1 | ||||
1Department of removable prosthodontics, Faculty of Dental medicine, (Assiut, Boys), Al-Azhar University, Egypt. | ||||
2Department of removable prosthodontics, Faculty of Dental medicine, (Assiut, Boys), Al-Azhar University, Egypt | ||||
Abstract | ||||
Aim: estimate flexural strength of strengthened denture base resin by different concentrations of Zirconium oxide nanoparticles (Zro2 Nps), Aluminum oxide nanoparticles (Al2o3 Nps) and Titanium oxide nanoparticles (Tio2 Nps). Subjects and methods: fifty sample were got ready to experimentation of flexural strength together with dimensions 65 length x 10 width x 2.5mm thickness and then these samples were split into 4 series (A, B, C, D) and these groups then partitioned to 3 sub collections (1, 2, and 3) of 5 specimens for each group according to the ratio of Zro2Nps, Al2o3 Nps and Tio2 Nps which were (1%, 2% and 3%) for each type of nanoparticles that were added to heat-cured Poly methyl methacrylate (PMMA). Results: Regardless to metal oxide type, totally the highest mean value was recorded for control group < /div> (77.96 MPa). The difference between groups was statistically significant as indicated by ANOVA test (p=<0.0001<0.05) for flexural strength. Conclusions: It was found that there is slight decreasing in transverse strength of PMMA for all concentrations added of Zro2Nps, Al2o3 Nps and Tio2 Nps when compared to control group. | ||||
Keywords | ||||
Reinforced of denture base acrylic resin; flexural strength; Zirconium oxide; Aluminum oxide; Titanium oxide nanoparticles | ||||