EFFECT OF SIC CONTENT ON DRY SLIDING WEAR BEHAVIOR OF NANOSIZED SIC(P)/CU COMPOSITES | ||||
Journal of Al-Azhar University Engineering Sector | ||||
Article 23, Volume 13, Issue 49, October 2018, Page 1260-1267 PDF (590.42 K) | ||||
Document Type: Original Article | ||||
DOI: 10.21608/auej.2018.18937 | ||||
View on SCiNiTO | ||||
Authors | ||||
M Abd-Elmonem Metwally1; H A.Fattah* 2; M Ghanem3; I Batanony4 | ||||
1Egyption Natual Gas Company ( GASCO) | ||||
2Mining and Pet. Dept, Faculty of Engineering, , Al-Azhar University | ||||
3Industrial Education, Suez University, Egypt | ||||
4Mech.Eng.Dept.Faculty of Engineering, Al-Azhar University | ||||
Abstract | ||||
In this study, the wear behavior of nano Cu and SiC(p)/Cu composites powders with different weight percentages of SiC particles was investigated under pin on disc equipment at 8–20 N load and 0.83-3.25 sliding speed. The composites were produced via powder metallurgy (PM) route. The results revealed that the wear resistance of SiC(p)/Cu composites increased with increasing SiC content to 20 vol %. Beyond this value the wear resistance decreased but still more than the unreinforced sample. Moreover, the investigation on worn surfaces was done to understand wear mechanism. | ||||
Keywords | ||||
Cu alloys; Composite materials; Sic; Wear; Worn | ||||