CHARACTERIZATION OF AL-SI-NI TERNARY ALLOY SYNTHESIS FROM REDUCTION OF SODIUM-FLUOSILICATE AND NICKEL OXIDE

Farag, Mohammed; Kh, Moatasem; Atlam, A A; Omran, A M

doi:10.21608/auej.2018.18989

	CHARACTERIZATION OF AL-SI-NI TERNARY ALLOY SYNTHESIS FROM REDUCTION OF SODIUM-FLUOSILICATE AND NICKEL OXIDE
Journal of Al-Azhar University Engineering Sector
Article 30, Volume 13, Issue 48, July 2018, Page 1100-1108 PDF (562.7 K)
Document Type: Original Article
DOI: 10.21608/auej.2018.18989
View on SCiNiTO
Authors
Mohammed Farag¹; Moatasem Kh¹; A A Atlam²; A M Omran¹
¹Mining and Metallurgical Engineering Department, Faculty of Engineering, Al-Azhar University, Qena- Egypt
²Mining and Petroleum Engineering, Faculty of Engineering, Al_Azhar University, Cairo- Egypt. Corresponding author
Abstract
A new Al-Si-Ni high-temperature processed alloy has been obtained using sodium fluosilicate as a source of Si and nickel oxide as a source of Ni. Throughout the study, we tested the optimum parameters affecting the preparation of Al-Si-Ni ternary alloy; bath temperature, Na₂SiF₆/Al_total w.t ratio, Ni₂O₃/Al_total and reaction time. The optimum processing parameters are; temperature 950^oC, Na₂SiF₆/Al_total wt. ratio is 1, Ni₂O₃/Al_total wt. ratio is 0.082 and reaction time is 25 min. Some tests such as chemical analysis, X-ray diffraction and microstructure examination were carried out on the produced alloys. The obtained results indicate that the produced alloys containing up to 10.75% Si and 2.86 Ni in the form of Al₃Ni. The presence of eutectic Si and eutectic Al₃Ni could form interconnected system and it can be used as high-performance alloys at elevated temperature.
Keywords
words: High temperature alloys; Sodium fluosilicate; Al-Si-Ni ternary alloy; Nickel oxide