Time effect of graphene coating in between metallic layers of Copper-Nickel on corrosion behavior for carbon steel in saline water | ||||
| Journal of Petroleum and Mining Engineering | ||||
| Article 8, Volume 23, Issue 2, December 2021, Page 70-80 PDF (1.05 MB) | ||||
| Document Type: Original Article | ||||
| DOI: 10.21608/jpme.2021.100613.1099 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
ashraf abd elrazek atia  1; Mosaad Mohamed Sadawy2; Amr Kandil3; Ahmed Aly Atlam4
| ||||
| 1Higher Technological Institute, 10th of Ramadan City, Egypt | ||||
| 2Mining and Petroleum dept. - Faculty of Engineering- Alazhar University | ||||
| 3Mining and petroleum dept.- Faculty of Engineering-Alazhar University | ||||
| 4Al-Azhar University, Faculty of Engineering, Mining and Pet. Dept., Nasr City, P.O. Box 11371 | ||||
| Abstract | ||||
| The study was an experimental investigation for Time 10 min, 20 min, and 30 min effect of graphene coating in between metallic layers of Copper-Nickel on corrosion behavior for carbon steel in saline water. And Surface finishing for substrates was P320, P600, and P1200 mesh until a mirror shiny surface before coated by metallic layers Cu – Cu – Ni reinforced with concentrations 0.25, 0.5, 1and 2 g/L graphene. First, X-ray diffraction (XRD), electron microscopy (SEM) associated with carbon steel & graphene, and Microscopic test for coated specimens. The techniques were performed to study the effect of saline water (3.5%) on corrosion behaviors. Open circuit potential Eoc, Tafel polarization, cyclic potentiodynamic polarization, and impedance spectroscopy EIS tests. The types of corrosion were pitting corrosion, where the highest protection against corrosion was at 20 min with concentration 1 g/L graphene coating with P600 and P320 mesh. The time increasing led to increasing in Protection Efficiency (PE%), decreasing for Corrosion Rates (mpy), increasing for Polarization Resistance (Rp), and decreasing for Porosity Percentage (PP%).Between metallic layers coating reinforced with concentrations 0.25, 0.5, 1and 2 g/L graphene. | ||||
| Keywords | ||||
| Carbon steel; Electrolyte; Cu –Ni -Graphene oxide coating; Corrosion behavior | ||||
|