Flocculation Activity of Grafted Chitosan for Water Treatment | ||||
| Egyptian Journal of Chemistry | ||||
| Article 22, Volume 65, Issue 12, December 2022, Page 227-237 PDF (645.35 K) | ||||
| Document Type: Original Article | ||||
| DOI: 10.21608/ejchem.2022.119028.5352 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
Raedah Alatawi1; Abeer Abdulaziz Bukhari2; Hanan Elsayed3; Uzma Faridi4; Sanaa Khali5; Wael Mohammed  2
| ||||
| 1Department of Chemistry, Faculty of Science, University of Tabuk, Tabuk 71421, Saudi Arabia | ||||
| 2Department of Chemistry, Faculty of Science, University of Tabuk, Saudia Arabia | ||||
| 3Food Science Department, Faculty of Agricultural, Ain Shams University, Cairo, Egypt. | ||||
| 4Biochemistry department, Faculty of Science, University of Tabuk, Tabuk 71421, Saudi Arabia | ||||
| 5Chemistry Department, Alwajh-College, University of Tabuk, Tabuk, Saudi Arabia | ||||
| Abstract | ||||
| Chitosan was grafted with dimethylamino ethyl methacrylate monomer, and with dimethylamine ethyl methacrylate-acrylic acid monomers. The obtained chitosan poly dimethylamine ethyl methacrylate [I] as well as Chitosan poly- dimethylamine ethyl methacrylate-acrylic acid [II] hybrids were evaluated in flocculation performance of kaolin suspension and also in the clarification behavior of treated raw water when combined with alum. The polymerization was carried out using potassium persulphate/sodium bisulphite redox initiation system at temperature of 60OC for 3 hours. The obtained two grafted samples were characterized using FTIR: thermal properties expressed as thermogravemetric analysis (TGA) and differential scanning calorimeter (DSC) as well as X-ray. The water clarification for kaolin suspension was evaluated for the two obtained hybrid polymers with respect to the pH, polymer dosage, and settling time. The combination between the prepared hybrid and alum was also investigated. The results show that the grafted chitosan copolymers I & II exhibit thermal stability. The best flocculation for two prepared hybrid I & II were observed as pH 6.5 and dosage concentration of 1 ppm with recorded turbidity of 3.01 & 2.66 NTU. The best flocculation was observed for native chitosan at pH 7.5 and 4.85 NTU. Combination between 25 ppm alum with 0.5 of each of I & II induce more water clarification with turbidity values of 1.84 & 1.65. | ||||
| Keywords | ||||
| Flocculation; chitosan; characterization; kaolin; water treatment | ||||
|