The Effect of Addition Nanosilica on Mechanical Properties of Poly (methyl methacrylate) | ||||
Egyptian Journal of Chemistry | ||||
Volume 66, Issue 8, August 2023, Page 339-345 PDF (950.57 K) | ||||
Document Type: Original Article | ||||
DOI: 10.21608/ejchem.2022.120635.5419 | ||||
View on SCiNiTO | ||||
Authors | ||||
mohammed amin alibadi 1; S. M. Thahab2; Iman Jabber Alshaibani1 | ||||
1Materials Engineering Department, Faculty of Engineering, University of Kufa, Najaf, Iraq | ||||
2Electronics and Communication Department, Faculty of Engineering, University of Kufa, Najaf, IRAQ | ||||
Abstract | ||||
This research focuses on using silica nanoparticles prepared from rice husk ash and commercial nano silica to successfully produce PMMA/Sio2 nanocomposite with various Sio2 weight loadings (0.05, 0.1, and 0.15 % wt.). The samples were manufactured by utilizing an ultrasonic machine and a solution mixing. The characterization of the resulting PMMA/Sio2 nanocomposites were investigated using hardness, impact testing, flexural strength, and SEM.. The results showed that the best value percentage of RH is (0.05wt%) for Impact strength and (0.05wt%) for flexural strength, which gives the highest strength .and The best value percentages that gives the highest strengths for NP is (0.05wt%) for Impact strength and (0.1wt%) for flexural strength. SEM were also tested to find the structure of Sio2 and dispersion quality. | ||||
Keywords | ||||
Polymethylmethacrylate; nanosilica; impact; hardness; flexural transverse; SEM | ||||