Evaluation of Microtensile Bond Strength, Microleakage Pattern and Micromorphological Analysis of New Functional Monomer-Based Universal Adhesive Tooth Interface | ||||
Mansoura Journal of Dentistry | ||||
Volume 9, Issue 4, December 2022, Page 198-204 PDF (462.86 K) | ||||
Document Type: Original Article | ||||
DOI: 10.21608/mjd.2022.150206.1069 | ||||
View on SCiNiTO | ||||
Abstract | ||||
Objective: This study was intended to evaluate the micro tensile bond strength (μTBS), micro leakage pattern, and micro morphological analysis of new 10-MDP-based universal adhesive/tooth interface and compare it with other two 10-MDP-based adhesive systems before and after storage. Materials and Methods: Two Universal adhesives (Single Bond Universal Adhesive and Ambar Universal) and one all-in-one adhesive (CLEARFIL S3BOND) were used. A total of 102 permanent human molars were used in this study. The teeth were randomly divided into three groups (n=34) according to the type of used adhesive; Ambar Universal (AU), CLEARFIL S3BOND (CTS), and Single Bond Universal (SBU). Each group was then subdivided into two subgroups (n=17) according to the time of testing. Results: It was shown that changing time had no statistically significant effect on µTBS (p > 0.05); however, changing group had a statistically significant effect (p < 0.05). Additionally, the combination of changes in group and time had no statistically significant effect on the µTBS (p > 0.05). Furthermore, it was shown that changing group or time did not significantly affect the micro leakage score. Finally, a slight difference was observed between the studied groups mainly in the resin tags; however, all adhesives showed a loss of resin tags after thermo cycling.Conclusions: The new 10-MDP-based universal adhesive had lower bond strength to dentin than the other tested adhesives. However, the new 10-MDP-based universal adhesive/tooth interface had relatively similar micro leakage patterns and micro morphological features in comparison with the other tested adhesives. | ||||
Keywords | ||||
Keywords: universal adhesive; dentin; bond strength; 10-MDP; functional monomer | ||||