FATIGUE RESISTANCE, FRACTURE STRENGTH AND MARGINAL INTEGRITY OF THREE TYPES OF CAD/CAM HYBRID CERAMIC CROWNS
abd elkader el-aidy, A., Shebl kassem, A., Elgabrouny, M., abd elhamid, T. (2023). FATIGUE RESISTANCE, FRACTURE STRENGTH AND MARGINAL INTEGRITY OF THREE TYPES OF CAD/CAM HYBRID CERAMIC CROWNS. EKB Journal Management System, 69(1), 523-531. doi: 10.21608/edj.2022.168765.2296
aya abd elkader el-aidy; Amr Shebl kassem; Mosaad Elgabrouny; tarek abd elhamid. "FATIGUE RESISTANCE, FRACTURE STRENGTH AND MARGINAL INTEGRITY OF THREE TYPES OF CAD/CAM HYBRID CERAMIC CROWNS". EKB Journal Management System, 69, 1, 2023, 523-531. doi: 10.21608/edj.2022.168765.2296
abd elkader el-aidy, A., Shebl kassem, A., Elgabrouny, M., abd elhamid, T. (2023). 'FATIGUE RESISTANCE, FRACTURE STRENGTH AND MARGINAL INTEGRITY OF THREE TYPES OF CAD/CAM HYBRID CERAMIC CROWNS', EKB Journal Management System, 69(1), pp. 523-531. doi: 10.21608/edj.2022.168765.2296
abd elkader el-aidy, A., Shebl kassem, A., Elgabrouny, M., abd elhamid, T. FATIGUE RESISTANCE, FRACTURE STRENGTH AND MARGINAL INTEGRITY OF THREE TYPES OF CAD/CAM HYBRID CERAMIC CROWNS. EKB Journal Management System, 2023; 69(1): 523-531. doi: 10.21608/edj.2022.168765.2296

FATIGUE RESISTANCE, FRACTURE STRENGTH AND MARGINAL INTEGRITY OF THREE TYPES OF CAD/CAM HYBRID CERAMIC CROWNS

Egyptian Dental Journal
Article 9, Volume 69, Issue 1 - Serial Number 4, January 2023, Page 523-531  XML PDF (528.14 K)
Document Type: Original Article
DOI: 10.21608/edj.2022.168765.2296
View on SCiNiTO View on SCiNiTO
Authors
aya abd elkader el-aidyorcid 1; Amr Shebl kassem email orcid 2; Mosaad Elgabrounyorcid 3; tarek abd elhamidorcid 2
1Assistant Lecturer, Department of Crown and Bridge, Faculty of Dentistry, Suez-Canal University, Ismailia, Egypt
2Lecturer, Department of Crown and Bridge, Faculty of Dentistry, Suez-Canal University, Ismailia, Egypt
3Professor, Department of Crown and Bridge, Faculty of Dentistry, Suez-Canal University, Ismailia, Egypt
Abstract
Aim:To assess fatigue resistance,fracture strength and marginal integrity of three different CAD/CAM resin-based ceramic materials.Materials & methods:A maxillary premolar tooth was prepared to receive an all-ceramic crown, scanned with Omnicam intraoral scanner.A STL file was transferred to Formlabs 3D-printer to print fifteen resin dies.One die was scanned with Cerec Omnicam and fifteen hybrid ceramic crowns were milled with Cerec MCXL milling machine.Crowns were divided into three groups (n=5) according to their material type;group A (Vita Enamic),group B (Brilliant Crios) and group C (Shofu Hc).Crowns vertical marginal gaps were measured using a USB digital microscope.Crowns were bonded using Panavia F2.0 adhesive resin cement then their vertical marginal gaps were remeasured.Thermocycling of the crowns was done for 5000 cycles and crows were subjected to fatigue using a chewing simulator by applying cyclic loading of 50 N for 250,000 cycles with a frequency of 1.6 Hz.Vertical marginal gaps of survived crowns were measured.Survived crowns were subjected to static load to fracture using a universal testing machine at a crosshead speed of 1 mm/min.Data were analyzed by one way ANOVA and Post Hoc Tests at p  0.05.Results:There was a statistically significant difference between mean vertical marginal gap of all groups where group C showed the highest mean vertical marginal gap through all stages;before or after bonding and after thermomechanical aging.All crowns survived fatigue testing.Group C showed the highest mean fracture strength followed by group A then Group B.Conclusions:Tested materials showed vertical marginal gaps, fatigue resistance and fracture strength within the clinically acceptable range
Keywords
Hybrid ceramics; Fatigue; Thermocycling; Marginal gap; CAD/CAM