Utilization of Kalapsha Kaolin to Prepare High Purity Alumina | ||||
| Egyptian Journal of Chemistry | ||||
| Article 11, Volume 62, Issue 9, September 2019, Page 1699-1712 PDF (1.62 MB) | ||||
| Document Type: Original Article | ||||
| DOI: 10.21608/ejchem.2019.10211.1670 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
Sohair Taha Aly  1; Ibrahim Ahmed Ibrahim2; Magdi Fouad Abadir3
| ||||
| 1Chemical Engineering Department, Egyptian Academy for Engineering and Advanced technology | ||||
| 2Material science department, Central Metallurgical Research and Development Institute, Cairo Egypt | ||||
| 3Chemical Engineering Department, Faculty of Engineering, Cairo University | ||||
| Abstract | ||||
| ABSTRACT Kalabsha kaolin was calcined at 700oC then treated with hydrochloric acid to produce aluminum chloride hexahydrate. The hexahydrate was obtained in crystalline form through injection of hydrogen chloride gas in saturated solution and purified on several steps to obtain alumina of high purity. Acid leaching conditions, namely, acid to kaolin stoichiometric ratio(S), reaction time (t) and reaction temperature (T) were optimized using surface response methodology. A maximum alumina recovery of 83.2% was predicted on using 1.4 stoichiometric acid to solid ratio, a reaction temperature of 104oC and a reaction time of 3 hours. This result was then assessed experimentally. The hexahydrate crystals obtained were subsequently purified in a three stage process to increase their purity to 99.961%. Calcination of these crystals for 4 hours at 1100oC produced highly crystalline alumina with purity 99.9%. | ||||
| Keywords | ||||
| KEYWORDS: Alumina; kaolin; Leaching; HCl; Statistical Study; crystallization; Calcination | ||||
|