Effect of adding chitosan nanoparticles on flexural strength and hardness of heat cured acrylic resin before and after thermo-cycling | ||||
| Egyptian Dental Journal | ||||
| Article 1, Volume 69, Issue 2 - Serial Number 4, April 2023, Page 1181-1187 PDF (1.09 MB) | ||||
| Document Type: Original Article | ||||
| DOI: 10.21608/edj.2023.178476.2366 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
Ali Bayiumy   1; mohammad elsokkary 2
| ||||
| 1Lecturer of Dental Materials, Faculty of Dentistry, Assiut University | ||||
| 2Lecturer of Prosthodontics, Faculty of Dentistry, Assiut University | ||||
| Abstract | ||||
| ABSTRACT: Objective: The aim of this study was to evaluate the effect of two concentrations of chitosan nanoparticles on the mechanical properties of heat polymerized acrylic resin before and after thermocycling. The tested parameters were flexural strength and hardness. Material and Methods: 120 specimens were prepared according to the specific dimension for each test (flexural strength and micro hardness) and distributed into - Before thermocycling (control, chitosan nanoparticles with concentration 0.3% and 0.5%) - After thermocycling (control, chitosan nanoparticles with concentration 0.3% and 0.5%) Results: Flexural strength and micro hardness were tested for both groups. The data was collected and statistically analyzed. Flexural strength was non-significantly increased for ratio of 0.3% chitosan nanoparticles in comparison to control before and after thermo cycling and significantly decreased for 0.5% chitosan nanoparticles before thermocycling and non-significant decrease after thermocycling in comparison to control For hardness showed non-significant decrease for both concentrations and significant decrease for control after thermocycling Conclusion: adding chitosan nanoparticles to heat cured acrylic resin increased the flexural strength for 0.3% ratio and non-significantly decreased for 0.5, while decreased non-significantly micro hardness for both concentrations. | ||||
| Keywords | ||||
| acrylic; Nano chitosan; flexural strength; hardness | ||||
|