STRESS ANALYSIS AND FAILURE RISK OF ENDODONTICALLY TREATED MOLARS RESTORED WITH THREE CAD/CAM MATERIALS OVER COMPOSITE CORE AND GLASS FIBER INSERTION
abo elhassan, R., ahmed, D., elkersh, N. (2023). STRESS ANALYSIS AND FAILURE RISK OF ENDODONTICALLY TREATED MOLARS RESTORED WITH THREE CAD/CAM MATERIALS OVER COMPOSITE CORE AND GLASS FIBER INSERTION. EKB Journal Management System, 69(2), 1529-1544. doi: 10.21608/edj.2023.200949.2493
rewaa abo elhassan; dwlat ahmed; noha elkersh. "STRESS ANALYSIS AND FAILURE RISK OF ENDODONTICALLY TREATED MOLARS RESTORED WITH THREE CAD/CAM MATERIALS OVER COMPOSITE CORE AND GLASS FIBER INSERTION". EKB Journal Management System, 69, 2, 2023, 1529-1544. doi: 10.21608/edj.2023.200949.2493
abo elhassan, R., ahmed, D., elkersh, N. (2023). 'STRESS ANALYSIS AND FAILURE RISK OF ENDODONTICALLY TREATED MOLARS RESTORED WITH THREE CAD/CAM MATERIALS OVER COMPOSITE CORE AND GLASS FIBER INSERTION', EKB Journal Management System, 69(2), pp. 1529-1544. doi: 10.21608/edj.2023.200949.2493
abo elhassan, R., ahmed, D., elkersh, N. STRESS ANALYSIS AND FAILURE RISK OF ENDODONTICALLY TREATED MOLARS RESTORED WITH THREE CAD/CAM MATERIALS OVER COMPOSITE CORE AND GLASS FIBER INSERTION. EKB Journal Management System, 2023; 69(2): 1529-1544. doi: 10.21608/edj.2023.200949.2493

STRESS ANALYSIS AND FAILURE RISK OF ENDODONTICALLY TREATED MOLARS RESTORED WITH THREE CAD/CAM MATERIALS OVER COMPOSITE CORE AND GLASS FIBER INSERTION

Egyptian Dental Journal
Article 33, Volume 69, Issue 2 - Serial Number 4, April 2023, Page 1529-1544  XML PDF (2.3 MB)
Document Type: Original Article
DOI: 10.21608/edj.2023.200949.2493
View on SCiNiTO View on SCiNiTO
Authors
rewaa abo elhassan email orcid 1; dwlat ahmedorcid 2; noha elkershorcid 3
1Lecturer of Fixed Prosthodontics, Faculty of Dentistry, Alexandria University
2Assistant Professor of Dental Biomaterials, Faculty of Dentistry Alexandria Univesity
3Lecturer of Oral and Maxillofacial Radiology, Faculty of Dentistry Alexandria University
Abstract
Objective: Evaluating the stress distribution pattern and failure risk of post retained crown restorations using e.max CAD), Lava ultimate, and ZirCAD restorative crown materials.
Materials & methods: Endodontically treated human molar with fiber post and composite core was digitized after CBCT, CAD software (Catia) were used to create FEA model imbedded in alveolar bone and 3 crown material: (1) EM; (2) LU; (3) ZC, A static components of 600 N loads were applied on the occlusal surface , analysis program by ANSYS 2021 were used for Finite element analysis (FEA) , calculated the VMs distributions values and the total deformation values to detect the failure risk.
Results: There was difference on both VMs values at restorative crown and the remaining tooth structure and the surrounding tissues. The results showed that the greater elasticity modulus of ZC restorative material was been proportional to the higher VMs distribution values. While the lower elasticity modulus of LU was proportional to the low VMs values and remaining tooth structure. VMs values of stress distribution on composite resin core and fiber post in the ZC model were lower than LU restorative material. For the total deformation values, the risk of failure of the three models was nearly the same.
Conclusions: LU showed lower stress distribution profile and superior mechanical response that grants LU to be used as a good dental restoration.