Economical Method for Synthesis A Nanocrystalline Chromia Doped Alumina Based Aluminum Foil Waste | ||||
The Bulletin Tabbin Institute for Metallurgical Studies (TIMS) | ||||
Volume 106, Issue 1, September 2017, Page 15-23 PDF (1.53 MB) | ||||
Document Type: Original research papers | ||||
DOI: 10.21608/tims.2017.299435 | ||||
View on SCiNiTO | ||||
Authors | ||||
A. R. Abdel-Aziem1; E. M. M. Ewais1; A. A. Mohamed2 | ||||
1Refractory and Ceramic Materials Division (RCMD), Central Metallurgical R&D Institute, P.O. 87 Helwan, 11421 Cairo, Egypt. | ||||
2Chemistry Department, Faculty of Science, Helwan University | ||||
Abstract | ||||
This study aims to synthesize a nanocrystalline alumina doped with chromia by using aluminum foil waste as a source of alumina and chromium nitrate non-hydrate as a source of chromia. Chromia doped alumina was prepared by co-precipitation method and fired at different temperatures. The co-precipitated powder formed thereby has been examined by XRD, FTIR and TEM techniques. X-Ray diffraction patterns show a good crystalline of the powder with very sharp and neat peaks at high temperatures more than 1000°C. The results of FTIR analysis confirmed the getting of solid solution of alumina chromia. TEM photographs show the good distribution of the particles, which have an average particle size of 1-3 nm at low temperature. | ||||
Keywords | ||||
Chromia doped alumina; Aluminum foil waste; Coprecipitation; TEM | ||||