MECHANICAL AND TRIBOLOGICAL PROPERTIES OF POLYMETHYL METHACRYLATE MATRIX REINFORCED WITH NOVEL HYBRID ORGANIC AND INORGANIC NANO-FILLERS. | ||||
| Journal of the Egyptian Society of Tribology | ||||
| Volume 20, Issue 3, July 2023, Page 40-62 PDF (1.29 MB) | ||||
| Document Type: Original Article | ||||
| DOI: 10.21608/jest.2023.308333 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
| A. El-Sayed M. Hassan1; Eman M. Ali1; M. N. El‑Sheikh1; M. Nafea M. Rohim1; Heba I. Elkhouly2 | ||||
| 1Mechanical Dept., Faculty of Technology and Education, Beni-Suef University, Beni-Suef, EGYPT. | ||||
| 2Department of Mechanical Engineering, Faculty of Engineering, Beni-Suef University, Beni‑Suef, EGYPT. | ||||
| Abstract | ||||
| Polymethyl methacrylate (PMMA) possesses favorable properties such as a valuable physical characteristic, low cost, and its ease and aesthetic fabrication. However, it suffers from low hardness and tribological properties in denture base applications. In this work, the mechanical and tribological properties of PMMA reinforced with organic, inorganic, and hybrid of organic/inorganic nanoparticles (NPs) were investigated. The used organic fillers were date seed (DS) NPs and inorganic fillers were titanium dioxide (TiO2) NPs. TiO2 and DS NPs were characterized by transmission electron microscope (TEM). PMMA-based non-hybrid and hybrid nanocomposites were fabricated by using a self-curing method. To fabricate the non-hybrid composites of C1 and C2, TiO2 and DS NPs were added at a constant weight fraction (wt. %) of 1.2 to PMMA, respectively. For manufacturing hybrid nanocomposites, C1 was reinforced by 0.1, 0.2, 0.3, 0.4, and 0.5 wt. % DS NPs. Also, C2 was reinforced with TiO2 NPs at the same loading content of 0.1, 0.2, 0.3, 0.4, and 0.5 wt. %. Unfilled PMMA, C1, C2, C1/0.4 wt. % DS NPs, and C2/0.4 wt. % TiO2 NPs were analyzed by Fourier transform infrared (FTIR) technique. Vickers hardness number (VHN), wear rate, and coefficient of friction (COF) tests were conducted to study the effect of hybrid NPs content on the mechanical and tribological properties of PMMA. The worn surfaces of rubbed specimens after the wear test were imaged by scanning electron microscope (SEM). The experimental results proved that the mechanical and tribological characteristics of unfilled PMMA were significantly improved at content of 1.2 wt. % DS and TiO2 NPs for C1 and C2, respectively. Hence, the hybrid nanocomposites that reinforced with 0.4 wt. % DS or TiO2 NPs recorded a distinct mechanical and tribological behavior among other filler content. Also, the hybrid nanocomposites of C2/0.4 wt. % TiO2 NPs showed significant improvement by 14.12, 16.66, and 2.96 % in the VHN, wear rate, and COF, respectively compared to the hybrid nanocomposites of C1/0.4 wt. % DS NPs. Finally, samples costing study proved that the unit cost of the hybrid nanocomposites of C2/0.4 wt. % TiO2 NPs is lower than that of the hybrid nanocomposites of C1/0.4 wt. % DS NPs by 47.61%. | ||||
| Keywords | ||||
| PMMA; Hybrid nanocomposites; Organic nanofillers; Inorganic nanofillers; Mechanical properties; Tribological properties | ||||
|