Preparation and Characterization of Low Cost Geopolymer Cement | ||||
Journal of Scientific Research in Science | ||||
Article 3, Volume 36, Issue 1, April 2019, Page 36-48 PDF (890.4 K) | ||||
Document Type: Original Article | ||||
DOI: 10.21608/jsrs.2019.30996 | ||||
View on SCiNiTO | ||||
Authors | ||||
ASHRAF RIZK* 1; ESSAM KISHAR1; D. A. AHMED2; MOHAMED KOHAIL3 | ||||
1Chemistry Department, Faculty of Women for Arts, Science and Education , Ain Shams University, Cairo, Egypt | ||||
2Chemistry Department, Faculty of Women for Arts, Science and Education , Ain Shams University, Cairo, Egypt , | ||||
3Structural Engineering Department, Faculty of Engineering Ain Shams University, Cairo, Egypt | ||||
Abstract | ||||
This paper presents the preparation and characterization of geopolymer cement. Sodium hydroxide with different percentage (4%, 6% and 8%) with sodium silicate (5%, 10% and 15%) of the mass of blast furnace slag are mixed to prepare the activator. The slag is mixed with the activator of different concentrations to prepare the geopolymer pastes. The physicochemical and mechanical properties of the hardened pastes cured in water at room temperature for different time intervals up to 90 days are measured.XRD of some selected samples are made. The results indicate that alkali content has significant effect on the physicochemical and mechanical properties of the hardened pastes. Compressive strength, combined water contents and bulk density increase while total porosity decrease with increasing alkali concentration. | ||||
Keywords | ||||
Alkali activated blast furnace slag; Compressive strength; Bulk density; total porosity and combined water | ||||