Antimicrobial Polypropylene Loaded by Cubic Cuprous Oxide Micro Particles | ||||
Egyptian Journal of Chemistry | ||||
Article 7, Volume 62, Issue 6, June 2019, Page 1047-1055 PDF (1.45 MB) | ||||
Document Type: Original Article | ||||
DOI: 10.21608/ejchem.2019.13001.1813 | ||||
View on SCiNiTO | ||||
Authors | ||||
Aziza Hussien1; Samiha Mahmoud Gawish 2; Sayeda El-Sayed Mosleh 3; Ameera Ramadan4; Galal Sayed5 | ||||
1National Research Centre, Textile Division, Dokki, Cairo, Egypt | ||||
2Textile Research Division, National Research Cetre | ||||
3Textile Division ,,National Research Centre, Dokki, Cairo | ||||
4Textile Division , National Research Centre ,Dokki, Cairo Egypt | ||||
5Ain Shams University - Faculty of Science | ||||
Abstract | ||||
Recently, nanotechnology of metals and their oxides is increased and became important for production of antimicrobial textiles. In situ synthesis of micro cuprous oxide particles (Cu2O), 1-30 mM/L onto non-woven polypropylene and study the antimicrobial activity were investigated. Cu2O Micro particles were prepared by chemical method using copper sulphate pentahydrate, sodium hydroxide and glucose as a reducing agent at 90o C for 2 hrs, followed by pad-dry-cure at 150ºC for 5min. Cu2O content onto PP was estimated before and after five washings and drying. Characterization of Cu2O Micro particles onto PP was done by XRD, SEM, EDX and which had revealed the presence of Cu2O micro particles in cubic shape at face dimeter 0.6-0.8μm. Characterization of polypropylene color after Cu2O treatment was determined at λmax 410 nm using the colorimetric data (L*, a*, b*, ΔE) and the color strength ( K/S). The antimicrobial activity of treated PP against pathogenic microbes such S. aureus, E. coliand C. albicans was evaluated after 24 hrs contact time and gave very good antimicrobial results. . | ||||
Keywords | ||||
Polypropylene (PP); Copper sulphate pentahydrate; Micro-cuprous oxide; Alkaline glucose; antimicrobial activity | ||||