Synthesis and Physicomechanical Studies of Nano ZnO Coated Textile fabrics | ||||
| Egyptian Journal of Chemistry | ||||
| Article 23, Volume 63, Issue 2, February 2020, Page 625-631 PDF (2.51 MB) | ||||
| Document Type: Original Article | ||||
| DOI: 10.21608/ejchem.2019.13725.1849 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
Soha Abd Alhalim1; Mostafa Mabrouk 2; Sayed Kanawy Ibrahim  3; Nermin H. Hamdy4; abdelrahim ramadan5
| ||||
| 1Apparel Department, Faculty of Applied Arts, Helwan University | ||||
| 2Refractories, Ceramics and Building materials Department | ||||
| 3National Research Centre, 30 El-Tahrir Street | ||||
| 4Home Economics Department, Faculty of Specific Education, Aswan University, Egypt | ||||
| 5Apparel Department, Faculty of Applied Arts, Helwan University, Egypt | ||||
| Abstract | ||||
| In the current study cotton fabric was in situ loaded with zinc oxide nanoparticles. Urea was used as a dispersion medium to transform zinc acetate salt into ZnONPs within the matrix of the cotton fabric. These cotton fabrics were characterized before and after loading of ZnONPs using DTA, FTIR, SEM coupled with EDX, tensile strength and air permeability in order to determine the effect of the in situ loaded ZnONPs on the thermal behavior, chemical integrity, microstructure, mechanical properties and air permeability (%) properties of the cotton fabrics. The obtained results reviled that presence of in situ loaded ZnONPs has a slight effect on the thermal behavior of the cotton fabrics. Also, presence of in situ loaded ZnONPs was confirmed by FTIR and SEM coupled with EDX techniques in form of dispersed aggregates within the cotton matrix. The physical properties of the in situ loaded ZnONPs were found to be dependent on the concentration of the ZnONPs. This treated cotton fabrics are recommended for biomedical applications. | ||||
| Keywords | ||||
| in situ; Physical properties; ZnO NPs; Cotton; biomedical applications | ||||
|