Impact of Collagen Crosslinkers on Improvement of Dentin Mechanical Properties after Root Canal Treatment | ||||
| Ain Shams Dental Journal | ||||
| Volume 37, Issue 1, March 2025, Page 319-327 PDF (1.14 MB) | ||||
| Document Type: Original articles | ||||
| DOI: 10.21608/asdj.2024.305538.1382 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
reem adel abdelgawad1; Mai H Ragab  2
| ||||
| 1Associate professor of Endodontics, suez canal university Assistant professor of endodontics, Taibah university | ||||
| 2Associate professor of Endodontics, Faculty of Dentistry, Suez Canal UniversityIsmailia | ||||
| Abstract | ||||
| Aim: The intent of this research was investigating the impact of Grape seed extract (GSE) and Tannic acid (TA) treatment on un-demineralized and demineralized dentin wall mechanical properties (microhardness, ultimate tensile strength, and flexural strength) after nonsurgical root canal treatment (NSRCT). Materials and methods: Sixty single-rooted extracted mature teeth were collected; their clinical crowns were removed to obtain 14-mm long root samples. Chemo-mechanical preparation was performed using Protaper-Next. Samples were divided randomly into Group I (un-demineralized), and Group II (demineralized). Groups were subdivided into three subgroups: Subgroup C (control), Subgroup G (GSE), and T (TA). Root samples were sectioned into halves longitudinally; one of each was used to evaluate microhardness and the other was used to create dentin slabs for flexural and ultimate tensile strengths evaluation. Results: Dentin demineralization reported a statistically significant negative impact on microhardness, flexural strength, and tensile strength (P-value <0.001). Dentin surface treatment using collagen crosslinkers reported a statistically significant positive impact on microhardness, flexural, and tensile strengths (P-value <0.001). Conclusion: Dentin surface final rinse using collagen crosslinkers (GSE and TA) may improve dentin mechanical properties; able to compensate for the decrease in dentin mechanical properties consequent to root canal treatment protocol. | ||||
| Keywords | ||||
| mechanical properties; Grape Seed Extract; Tannic Acid; collagen crosslinkers | ||||
|