Evaluation of Styrene/Butyl-Acrylate as Modifier Additive in (NBR) Compounds Vulcanizates | ||||
Egyptian Journal of Chemistry | ||||
Article 7, Volume 63, Issue 6, June 2020, Page 2063-2074 PDF (2.38 MB) | ||||
Document Type: Review Articles | ||||
DOI: 10.21608/ejchem.2019.10194.1972 | ||||
View on SCiNiTO | ||||
Authors | ||||
Adel khater 1; Ahmed Ismael2; Abbas yehia3; Mohamed El zayat4 | ||||
1department of polymer and pigment. National research centre | ||||
2National Research Centre, 30 El-Tahrir Street | ||||
3department of polymer and pigment. NRC | ||||
4department of physics, faculty of science, fayoum univeristy | ||||
Abstract | ||||
Styrene/butyl acrylate (SBt) was prepared using in-situ seed emulsion polymerization and precipitated in an excess of methanol. The prepared (SBt) was utilized as modifier additive for acrylonitrile–butadiene rubber (NBR) in different dosage i.e. 5 phr, 10 phr, 15 phr and 20 phr. The rheometric and the physicomechanical characteristics of the vulcanizates include tensile strength, elongation at break, and swelling in toluene and motor oil were studied at room temperature before and after aging at 90 oC for up to 7 days. Moreover, morphology and dielectric properties of the modified (NBR) vulcanizates were investigated as well. It was discovered that 20 phr of the Styrene/butyl acrylate (SBt) that incorporated with (NBR) has the highest physicomechanical characteristics as well as dielectric parameters. | ||||
Keywords | ||||
(NBR); (SBt); Dielectric properties; physicomechanical properties; Morphology | ||||