WEAR OF AL203 AND SIC PARTICLES REINFORCED ALUMINUM METAL MATRIX COMPOSITES FABRICATED BY PRESSING AND EXTRUSION | ||||
ERJ. Engineering Research Journal | ||||
Article 11, Volume 32, Issue 3, July 2009, Page 347-352 PDF (308.88 K) | ||||
Document Type: Original Article | ||||
DOI: 10.21608/erjm.2009.69353 | ||||
View on SCiNiTO | ||||
Author | ||||
M. Abd-Elhamid | ||||
Mechanical Design and Production Engineering Department, Faculty of Engineering, Zagazig UniveRsity, P.O. Box 44519, Zagazig, Egypt | ||||
Abstract | ||||
Dry sliding wear test of the A1 matrix with 15% ceramic reinforcements of AI2O3 or Sic particles were performed using a pin-on-disc machine. The composites weqe prepared by powder metallurgy techniques followed by extrusion process. Some factors such as loads and sliding time on the degree of wear of particulate metal matrix composites (PMMC) were carried out. Tests were performed under different loads at room temperature and constant sliding speed of 1.67 mls. Results indicate that the addition of A1203 and Sic particles in the AI matrix improve the wear resistance and hardness. PMMC with A1203 showed better performance than Sic reinforcement. SEM tests were carried out to reveal complex combination of wear mechanisms on the surface of the worn test specime | ||||
Keywords | ||||
: Aluminum matrix composites; Powder metallurgy; Ah03 and Sic particles; sliding wear | ||||
Statistics Article View: 79 PDF Download: 146 |
||||