Fabrication of Aluminum Matrix Nanocomposites by Hot Compaction | ||||
| Journal of Petroleum and Mining Engineering | ||||
| Article 3, Volume 22, Issue 1, June 2020, Page 16-20 PDF (418.6 K) | ||||
| Document Type: Original Article | ||||
| DOI: 10.21608/jpme.2020.14137.1006 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
Hossam M. Yehia  1; Mohamed Menisy2; S. Allam1; Saleh Kaytbay3
| ||||
| 1Faculty of Industrial Education, Helwan University, Cairo, Egypt | ||||
| 2Egypt Railways, Cairo, Egypt | ||||
| 3Mechanical Engineering Department, Benha Faculty of Engineering, Benha University, Egypt | ||||
| Abstract | ||||
| In this investigation, five aluminum matrix nanocomposites were obtained by the hot pressing at 800 MPa and 600 oC. The electrolysis coating technique was utilized to prepare the nano-nickel powder. The fabricated nanocomposites were characterized by studying their chemical composition, microstructure, hardness, and thermal expansion coefficient. The scanning electron microscope of the microstructure of the electroless nickel powder shows that the Ni particles have nano-size where it was less than 100 nm. The EDAX analysis of the fabricated composite that contains 25 wt. % (Al2O3) in different regions was established. No elements rather than Al, Cu, Ni, and O were observed. The hardness of the aluminum matrix increases as the content of the Al2O3 increases. In addition, the thermal expansion coefficient was reduced by increasing the Al2O3 content for reasons related to the low thermal expansion of the alumina reinforcement 7.2 x10-6 mm/oC compared with aluminum that has 23.1x10-6 mm/oC. | ||||
| Keywords | ||||
| aluminum matrix; Microstructure; hardness; Coefficient of Thermal Expansion | ||||
|