STABILITY OF ANTIMONY AND ITS ANODIC OXIDE FILM AGAINST CORROSION IN AQUEOUS SOLUTIONS | ||||
| Al-Azhar Bulletin of Science | ||||
| Article 2, Volume 20, Issue 1-A, June 2009, Page 15-24 PDF (951.93 K) | ||||
| Document Type: Original Article | ||||
| DOI: 10.21608/absb.2009.7540 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
A. A. EL MAGHRABY  1; A. S. MOGODA2
| ||||
| 1Chemistry department, Faculty of science, Cairo University, Giza, Egypt, | ||||
| 2Chemistry Department, Faculty of Science, Cairo University, Giza, Egypt. | ||||
| Abstract | ||||
| The open circuit potential and impedance measurements were used to investigate the corrosion behavior of antimony in 0.1M citric acid solution made to various pH values. The results showed that the antimony surface undergoes spontaneous corrosion in the citrate solutions. Also the properties of the anodic oxide film on antimony were examined by impedance technique. It was found that the antimony surface becomes more passive as the thickness of the anodic oxide film formed on antimony increase. The anodic oxide film on antimony behaves like a non- ideal capacitor. The stability of the anodic oxide film in the aqueous solutions was found to depend on the concentration of the formation medium for the anodic oxide. | ||||
| Keywords | ||||
| Antimony; oxide film; Corrosion | ||||
|