EVALUATION OF ACETAL RESIN AND COBALT–CHROMIUM CLASP DEFORMATION AND FATIGUE RESISTANCE IN REMOVABLE PARTIAL DENTURE CLASPS AN IN-VITRO STUDY | ||||
| Egyptian Dental Journal | ||||
| Article 1, Volume 63, Issue 3 - July (Fixed Prosthodontics, Dental Materials, Conservative Dentistry & Endodontics), July 2017, Page 2459-2464 PDF (897.45 K) | ||||
| Document Type: Original Article | ||||
| DOI: 10.21608/edj.2017.76062 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
| Mohamed Ahmed M. Helal1; Ibrahem Ali Abd El Rahman2; Hassan Mohamed Sakar3; Amr Salah El-Din Abd Elshafy Gomaa4; Mohamed Abbas5 | ||||
| 1Professor of Removable Prosthodontics, Faculty of Dental Medicine, Al-Azhar University. Boys Branch, Cairo, Egypt | ||||
| 2Dentist at the MOH, El-Mansoura, Egypt | ||||
| 3Assistant Professor of Removable Prosthodontics, Faculty of Dental Medicine, Al-Azhar University. Boys Branch, Cairo, Egypt. | ||||
| 4Lecturerof Removable Prosthodontics, Faculty of Dentistry, Al-Fayoum University, Fayoum, Egypt. | ||||
| 5Assistant Professor of Dental Material, Faculty of Dental Medicine, Al-Azhar University. Boys Branch, Cairo, Egypt | ||||
| Abstract | ||||
| Purpose: this study was aimed to evaluate the fatigue resistance (amount of clasp deformation) of acetal resin clasps and Cobalt-Chrome (Co-Cr) clasps after attachment/detachment cycles on abutment teeth with two different undercuts. Materials and Method: Twenty models were constructed by placing either an upper 1st premolar or upper 1st molar inside an acrylic rectangular block. Models were divided according to the abutment teeth into two groups (GI for 1st premolars group and GII for 1st molars group), 10 each. Each group was divided into two subgroups according the framework material, SGA for acetal resin clasp and SGC for Co-Cr clasp. Each testing models and its framework were mounted inside universal testing machine (Lloyd instruments Ltd, England). Cycling was carried out for each specimen till 2920 cycles. The data of the amount of clasp deformation after cycling were collected and tabulated. The data were subjected to statistical analysis using student’s t and paired t tests. Results: After 2920 cycles, the mean values and standard deviations of the clasp deformation for SGIC, SGIA, SGIIC and SGIIA were 0.0532±0.006, 0.007±0.003, 0.04323±0.0048 and 0.0275±0.004 mm, respectively. Conclusions: Co-Cr clasps had significant clasp deformation more than acetal resin clasps. Increase the thickness of cross section of the acetal resin clasp more than 1 mm was recommended in case of engaging undercut more than 0.25 mm. | ||||
|