PHYSICOCHEMICAL PROPERTIES OF SILICATE BASED BIOMATERIALS | ||||
| Egyptian Dental Journal | ||||
| Article 11, Volume 63, Issue 4 - October (Fixed Prosthodontics, Dental Materials, Conservative Dentistry & Endodontics), October 2017, Page 3427-3434 PDF (267.67 K) | ||||
| Document Type: Original Article | ||||
| DOI: 10.21608/edj.2017.76261 | ||||
 View on SCiNiTO | ||||
| Author | ||||
| Dalia Mukhtar Fayyad | ||||
| Associate Professor of Endodontics, Faculty of Dentistry, Suez Canal University. | ||||
| Abstract | ||||
| Aim: The purpose of this study was to compare solubility, pH, calcium ion release and setting time of Biodentine, Bioaggregate, and Bioactive glass. Materials and Methods: For the weight loss, pH changes and calcium ions release, the tested specimens were immersed in distilled water. The evaluations were performed at 1h, 24h and 7 d. The measurement of pH was done using digital pH meter. The measurement for Ca2+ ions release was done using atomic absorption spectrophotometry. The setting time was measured by using a Vicat apparatus. Data were analyzed by One Way ANOVA test and the Tukey post-hoc test at P ≤ 0.05. Results: Biodentine showed the greatest solubility, ultimate increase in pH, and highest calcium ion release at all time intervals and the shortest setting time. Bioactive glass showed alkalinity and moderate Ca2+ release after 1 h that were decreased by time. It also showed negative solubility. Conclusions: Biodentine and Bioaggregate favored proper physico-chemical properties except for solubility it was questionable. Bioactive glass is the best regarding solubility. Keywords: Bioactive glass, Bioaggregate, Biodentine , Physico-Chemical properties. | ||||
| Keywords | ||||
| (1) All materials tested recorded a favorable high pH and Ca2+ release. (2) Although Biodentine and Bioaggregate showed high solubility; Bioactive glass showed a negative one. (3) Biodentin has the shortest setting time | ||||
|
Statistics Article View: 121 PDF Download: 389 |
||||