Micro-shear Bond strength of Novel MDP Calcium- Fluoride Releasing Self-Adhesive Resin Cement after thermocycling | ||||
| Egyptian Dental Journal | ||||
| Article 51, Volume 64, Issue 1 - January (Fixed Prosthodontics, Dental Materials, Conservative Dentistry & Endodontics), January 2018, Page 821-833 PDF (2.25 MB) | ||||
| Document Type: Original Article | ||||
| DOI: 10.21608/edj.2018.78093 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
| Aliaa Mahrous1; Mohamed M Radwan2; Samah Mohamed Kamel3 | ||||
| 1Lecturer Fixed Prosthodontics Department, Faculty of Dentistry, Fayoum University, Egypt | ||||
| 2Lecturer Fixed Prosthodontics Department, Faculty of Dentistry, Beni Suaf University, Egypt | ||||
| 3Lecturer Oral Biology, Faculty of Dentistry, Modern Science and Arts University (MSA), Egypt | ||||
| Abstract | ||||
| Purpose: The purpose of the present study was to investigate the micro-shear bond strength and failure mode of novel “MDP calcium-fluoride releasing” self-adhesive resin cement (TheraCem) with tooth structure (enamel& dentin) and yttrium stabilized zirconia after thermocycling and comparing the results with universal “non-containing MDP” self-adhesive resin cement (Relay X Unicem as a control) Materials and Methods: Enamel and dentin specimens (20 discs each) were obtained by using diamond saw (IsoMet 4000 linear Precision saw, Buehler, USA) with copious water coolant. Twenty zirconia plates were obtained from IPS e.max ZirCad blocks (Ivoclar Vivadent, Schaan, Liechtenstein) and sintered in an inFire HTC speed high-temperature furnace (Sirona Dental System GmbH, Germany). Micro resin cylinders were created on the bonded surface and filled with the tested cements (n= 10 /substrate) group A (control) using non-containing MDP self-adhesive cement Relay X Unicem (3M ESPE) while group B (tested cement) using MDP calcium-fluoride releasing self-Adhesive resin cement TheraCem (BISCO, Schaumburg, Illinois, USA). Cements were left to self-cure for 5 minutes. All the specimens were thermocycled for 5,000 cycles (Thermocycler 1100 SD Mechatronik, GmbH). Micro-shear bond strength was measured using universal testing machine and debonded surfaces were examined for failure mode analysis with all morphological and ultrastructure changes using Scanning Electron Microscope (Quanta 250 Field Emission Gun, Netherlands) attached with EDX Unit (Energy Dispersive X-ray Analyses). The results were statistically analysed. Results: TheraCem (tested cement) had a slightly higher (mean±SD) µ-SBS (Mpa) value than RelyX (control) (18.96±4.36, 12.18±3.13; respectively) (P=0.177). Within enamel, TheraCem (6.46±1.37) had a significantly higher (mean±SD) µ-SBS (Mpa) value than RelyX (3.04±0.99) (P=0.002). Similarly, TheraCem in dentine (10.67±1.27) had a significantly higher (mean±SD) than RelyX (6.46±1.74) (P=0.014). As for zirconia, TheraCem (39.76±1.18) had a significantly higher (mean±SD) µ-SBS (Mpa) than RelyX (27.04±1.92) (P<0.001) Conclusion: using MDP calcium-fluoride releasing self-adhesive resin cement (TheraCem) may improve bond strength to all tested substrates (enamel, dentin and zirconia). Clinical significant: TheraCem self-adhesive resin cement can be considered as promising cement for many clinicians. Further clinical studies are required to provide long term clinical success data. | ||||
| Keywords | ||||
| TheraCem self-adhesive; MDP Calcium-fluoride Releasing adhesives; Relay X Unicem; enamel; Dentin; Zirconia; thermocycling; Micro-shear bond strength; failure mode | ||||
|