Enamel etching with an erbium, chromium: yttriumscandium- gallium-garnet laser system versus coventional acid etching technique in bonding metallic brackets | ||||
| Egyptian Orthodontic Journal | ||||
| Article 5, Volume 46, December 2014, December 2014, Page 75-93 PDF (3.05 MB) | ||||
| Document Type: Original Article | ||||
| DOI: 10.21608/eos.2014.78900 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
| Hanady Samih1; Khaled Aboul Azm2; Maha Abd El-Motie3 | ||||
| 1Orthodontics Department, Faculty of Dentistry, Suez Canal University, Ismailia, Egypt | ||||
| 2Orthodontics Department, Faculty of Dentistry, Pharos University, Alexandria, Egypt | ||||
| 3Dental Biomaterials Department, Faculty of Dentistry, Alexandria University, Egypt | ||||
| Abstract | ||||
| Introduction: The purpose of this study was to compare the shear bond strength of orthodontic brackets bonded to enamel etched with Er,Cr:YSGG laser at three different power outputs versus conventional acid etch. Materials and methods: Eighty-eight human premolars extracted for orthodontic purpose were used and were randomly divided into four equal groups according to enamel conditioning method. Enamel was etched with Er,Cr:YSGG laser system operated at one of three power outputs (1.5W, 2.0W and 2.5W) and with 37% orthophosphoric acid. Metal brackets were bonded to the etched enamel of eighty teeth using Transbond Plus adhesive material. The etched enamel surfaces of two teeth from each group were examined under scanning electron microscope (SEM). The shear bond strength was measured for all the groups using universal testing machine. The amount of remaining adhesive material on the teeth surface was determined using adhesive remnant index (ARI) scored from 0 to 3. Results: The means and standard deviations of shear bond strength for acid-etch group, 1.5W laser group, 2W laser group and 2.5W laser group were 9.60 ± 0.71, 7.22 ± 0.78, 11.68 ± 0.83 and 12.43 ± 0.71, respectively. The findings were confirmed by the scanning electron microscope. The evaluation of adhesive remnant index scores showed significant difference in bond failure site between all laser etched groups and acid etched group. There was more adhesive left on the enamel surface etched with acid than with laser. Conclusion: The mean shear bond strength and enamel etching with Er,Cr:YSGG laser at 2W power output for 20 seconds is clinically acceptable and comparable with conventional acid-etch. It can be considered as an alternative to acid-etch technique. | ||||
|
Statistics Article View: 48 PDF Download: 206 |
||||