EFFECT OF DIFFERENT REPAIR PROTOCOLS ON BOND STRENGTH TO DIRECT AND INDIRECT RESIN COMPOSITE | ||||
| Egyptian Dental Journal | ||||
| Article 20, Volume 62, Issue 1 - January (Part 3), January 2016, Page 747-756 PDF (1.16 MB) | ||||
| Document Type: Original Article | ||||
| DOI: 10.21608/edj.2016.95101 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
| Shereen Assem El-Sherif; Mohamed Riad Farid; Mohamed Fouad Haridy | ||||
| Department of Operative Dentistry, Cairo University, Cairo, Egypt | ||||
| Abstract | ||||
| Objective: This study was carried out to investigate the effect of different surface treatment protocols on bond strength of nano-composite as a repair material to two types of resin composite either direct composite or indirect resin composite blocks for CEREC system. Materials and methods: Total of 80 composite discs were prepared and were divided into two main groups (40 each) according to the type of composite used (C), nano-filled composite (C1) and composite blocks for CEREC system (C2). All specimens were aged for one month in a distilled water solution at 370C. Each group was sub-divided into four subgroups (10 each) according to the surface treatment protocol (T) that was done on the discs, either no treatment (T0) (control), application of Ortho phosphoric acid (T1), Hydrofluoric acid (T2) and Sandblasting(T3) . Each sub group was subdivided into two classes (5 each) according to silane application (S1) or without (S0). Nanofilled resin composite (Filtek Z350 XT, 3M ESPE) was used as a repair material. Microshear bond strength testing (μ-SBS) was done using Universal testing machine. Failure modes of the fractured specimens were analyzed using scanning electron microscope (SEM). μ-SBS results were analyzed using ANOVA, Tukey’s post-hoc and Student t-tests. Results: The indirect resin composite of the hydrofluoric acid group with silane showed the highest µ-Shear bond strength mean value (31.35±5.1) while the direct composite of the etchant group with no silane showed the lowest µ-Shear bond strength mean value (20.8±4.5). Regarding the composite type, C2 recorded statistically significant (P<0.05) higher µ-shear bond strength mean value (27.05±6.1 MPa) than C1 (23.82±6.2 MPa). Regarding the surface treatment, T3 recorded statistically non-significant (P>0.05) highest µ-shear bond strength mean value (26.72±0.78 MPa) followed by T1 (25.77±2.55 MPa) then T2 (24.71±1.44 MPa) while T0 recorded statistically non- significant (P>0.05) lowest µ-shear bond strength mean value (24.54±1.7 MPa). Regarding the silane application, S1 recorded statistically non-significant (P>0.05) higher µ-shear bond strength mean value (26.28±1.57MPa) than S0(24.59±1.66MPa). Conclusions: The Cojet treatment of the resin composite improved the bond strength of different types of resin composite .The type of resin composite used for repair influences the bond strength to the repaired resin composite. Silane application to repaired resin composite affects the bond strength to it with different treatment protocols. | ||||
| Keywords | ||||
| Computer-aided design/computer-aided manufacturing esthetic blocks; nano- filled resin composite; microshear bond strength; repair; scanning electron microscopy; silane | ||||
|
Statistics Article View: 140 PDF Download: 201 |
||||