Retanning agent for chrome tanned leather based on modern technique of emulsion polymers | ||||
Egyptian Journal of Chemistry | ||||
Article 47, Volume 64, Issue 1, January 2021, Page 503-516 PDF (1.13 MB) | ||||
Document Type: Review Articles | ||||
DOI: 10.21608/ejchem.2020.29577.2636 | ||||
View on SCiNiTO | ||||
Authors | ||||
Farouk Abd El-Monem 1; Ahmed I. Hussen2; H. Abd El-Wahab1; EL-Shahat H.A. Nashy3; A. M. Naser1 | ||||
1Chemistry Department, Faculty of Science Alazhar University | ||||
2Polymers and Pigments Dept. National Research Centre, Dokki, Cairo, Egypt. | ||||
3Chemistry of Tanning Materials and Leather Technology Dept. National Research Centre, Dokki, Cairo, Egypt. | ||||
Abstract | ||||
Retanning process aims at filling up of the meatuses of the already tanned leather through the incorporation of vegetable or synthetic tannins or polymer (resins) with the aim of giving more fullness and improving to the final product. In this research, poly(methyl methacrylate-co-butyl acrylate) emulsion was prepared in situ with nano-silica in order to be used as a modern retanning agent of chrome tanned leather to totally replace chrome salt and to enhance physical, thermal shrinkage, and mechanical properties of the final tanned leather as well as to reduce the environmental impact of chrome tanning effluent. Polymer/nano-silica hybrid emulsions were prepared via in situ seed emulsion polymerisation. The prepared polymers were characterised for solid content, molecular weight, viscosity, drying time, minimum film-forming temperature (MFFT) and microstructures (via TEM). The mechanical, shrinkage, thermal and surface morphological (by SEM) properties of the treated samples were also investigated. The influence of the increase in the content of organic nano-silica on the properties of the retanned leather were also discussed. | ||||
Keywords | ||||
emulsion polymer; reactive surfactants; nanosilica; retanning agent; chromium uptake; chrome tanned leather | ||||