Flammability Properties of Polyvinyl Alcohol Containing New Flame Retardant System | ||||
| Egyptian Journal of Chemistry | ||||
| Article 45, Volume 64, Issue 10, October 2021, Page 5863-5870 PDF (905.98 K) | ||||
| Document Type: Original Article | ||||
| DOI: 10.21608/ejchem.2021.71259.3568 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
Ghada Makhlouf1; Aksam Abdelkhalik   2; randa Naser3; Mohamed Hassan4
| ||||
| 1chemical metrology department, national institute of standard | ||||
| 2chemistry department, national institute of standard | ||||
| 3Reference material laboratory, National Institute of Standards | ||||
| 4Saudi Standards, Metrology and Quality Organization | ||||
| Abstract | ||||
| In this work, graphite (G), ammonium iron (II) sulfate (AFS) and aluminium nitrate were added to polyvinyl alcohol (PVA) at 25% loading level to improve its flame retardancy. In addition, PVA/(G+AFS+AN) composite was prepared. The flammability and smoke density of PVA composites were evaluated by UL94 flame chamber, limiting oxygen index (LOI) and smoke density chamber. Vertical flame spread test (UL94V) indicated that PVA composites achieved V0 class in PVA/(G+AFS+AN)and PVA/AFS samples. Horizontal burning rate (UL94H) data showed that PVA composites achieved H0 class. LOI of PVA was enhanced from 19.1% to 21.3%, 25.2%, 26.1% and 27.2% in PVA/G, PVA/AN, PVA/AFS and PVA/(G+AFS+AN)composites, respectively. The maximum specific optical density (Dsmax) of PVA was decreased in all PVA composites due to the formation of protective char layer on polymer surface. The maximum reduction in Dsmax value of PVA was 64% and it was observed in PVA/(G+AFS+AN). XRD analysis of char residue after smoke density test of PVA/(G+AFS+AN) indicated the presence of coquimbite phase, graphite and magnetite in the char residue. Thermogravimetric analysis (TGA) data of PVA and PVA/(G+AFS+AN) composite showed that the new flame-retardant system improved the thermal stability of neat polymer and the temperatures at which 50% (T50%) weight loss takes place were greatly enhanced. In addition, the char residue at 750 ℃ was increased. | ||||
| Keywords | ||||
| PVA; graphite; smoke density; ammonium iron (II) sulfate; aluminium nitrate | ||||
|