The Effect of Addition Graphite Filler on Mechanical Properties of Epoxy Material | ||||
| Egyptian Journal of Chemistry | ||||
| Article 35, Volume 64, Issue 10, October 2021, Page 5747-5754 PDF (583.11 K) | ||||
| Document Type: Original Article | ||||
| DOI: 10.21608/ejchem.2021.73645.3638 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
| Muayad Albozahid1; Abbas Ali Diwan2; Salih Abbas Habeeb3 | ||||
| 1Materials Engineering Department, Faculty of engineering, University of Kufa, Iraq. | ||||
| 2Nanotechnology and advanced material research unit, Faculty of engineering, University of Kufa, Iraq. | ||||
| 3Department of Polymers Engineering and Petrochemical Industries , Faculty of Materials Engineering, University of Babylon,Al-Hilla, Iraq | ||||
| Abstract | ||||
| The current study focuses on the effect of addition graphite filler on mechanical properties of epoxy material. The tensile and bending samples preparation of pure epoxy samples and epoxy with graphite powder with different weight ratio (0.15%, 1%, 2%wt) using ultrasonic dispersion device. The results showed the tensile stress and bending resistance were improved at (0.15%wt) and decreased at (1%, 2% wt), the decrease in tensile strength and bending resistance may be use of less time or low ultrasonic energy. The impact test improved at ratio (1%wt) and decreased at ratio (2% wt). There are decrease in hardness values with increase in graphite wieght fraction due to the lubricant effect of graphite flakes. In addiion of, the distribution of graphite can also affect this result where the penetrant was just on the surface. | ||||
| Keywords | ||||
| graphite; epoxy; tensile strength; impact; hardness | ||||
|