AC IMPEDANCE TECHNIQUE FOR ACCELERATED EVALUATION OF COATED STEEL SUBSTRATE | ||||
| Journal of Al-Azhar University Engineering Sector | ||||
| Article 33, Volume 11, Issue 39, April 2016, Page 825-843 PDF (2.6 MB) | ||||
| Document Type: Original Article | ||||
| DOI: 10.21608/auej.2016.19461 | ||||
 View on SCiNiTO | ||||
| Authors | ||||
| Emad Malallah; Adel Husain | ||||
| The Public Authority for Applied Education and Training Industrial Institute Shuwaikh, Welding Department , Kuwait Institute For Scientific Research | ||||
| Abstract | ||||
| The main aim of this preliminary research study was to introduce the Electrochemical Impedance Spectroscopy as a new instrument to be introduced to the Trainer of the Welding Department at Industrial Institute Shuwaikh as a training tool in the laboratory for the evaluation and screening of different coatings on steel substrate. In this respect a training and research investigation has been held on EIS at Construction and Building Materials CBM / KISR for Eng. Emad Malallah who is an Trainer at the Welding Department. The technical report consists of the following training sessions and research study: Literature Survey on different types of paints and protection mechanism Electrochemical Impedance Spectroscopy EIS; Theory and Lab Practice Experimental application of EIS on different generic type of coatings in order to understand the Impedance and capacitance response over a wide frequency range of 0.01 Hz to 100 KHz. The selected Paint system that has been investigated consists of; Clear Polyurethane Paints (C1&C2), HB Phosphate Primer (S1&S2), and Zinc Epoxy Polyamide (ZE); as well as un-painted bare steel substrate (BP&BN). The painted steel substrate was immersed in 3%NaCI solution for test duration ranging from 0 hrs. to 337 hrs. The AC Impedance results have indicated variation in the performance and deterioration behavior of the various paint system employed. The values of the paint film capacitance (Cc) and resistance (Ppo) were recorded experimentally from Nyquist plots. Photographic and SEM photomicrographic examination were obtained for the coated steel substrates. Finally, the EIS data obtained were used for ranking of the different selected paint systems according to the highest paint performance in Sodium Chloride solution and the paint surface free from the on sit of corrosion products, blisters or rust. The overall results have indicated that the best performance in terms of ranking were obtained for: ZE > S2 > CI ان الهدف الرئيسي من هذه الدراسة البحثية الأولية لتقديم الکهروکيميائية الممانعة الطيفية کأداة تدريبية جديدة يتم تعريفها للمتدرب من قسم اللحام في معهد الشويخ الصناعية لتقييم وفحص طبقات الطلاء المختلفة على الحديد الصلب. وفي هذا الصدد تم إجراء تدريب وتحقيق بحثي على EIS في مواد البناء والتصنيع CBM / في معهد الکويت للابحاث العلمية للمهندس عماد مال الله الذي يدرب في قسم اللحام. يتکون التقرير الفني من الدورات التدريبية والدراسة البحثية التالية: • مسح بحثي على الأنواع المختلفة من الدهانات وآلية الحماية المتوفرة. • الکهروکيميائية الممانعة الطيفية EIS؛ النظرية وسبل الممارسة بالمختبر. • التطبيق التجريبي ل EIS على الأنواع المختلفة من الطلاء من أجل فهم الممانعة والتصدي لنطاق واسع من الترددات 0.01 هرتز إلى 100 کيلو هيرتز. • يتکون نظام الطلاء المختار الذي تم التحقق منه من مادة البولي يوريثين الدهانات(C1&C2), HB وفوسفات التمهيدي (S1 & S2)، والزنک الايبوکسي مادة البولي أميد (ZE)؛ وکذلک الحديد الصلب الغير مطلي (BP وBN). وکان الحديد الصلب المطلي مغمور في ماء متکون من 3٪ ملح الطعام لمدة الاختبار التي تتراوح بين 0 ساعة إلى 337 ساعة. وقد أشارت نتائج AC الممانعة التباين في الأداء وتدهور سلوک مختلف نظام الطلاء المستخدمة. وأخيرا، تم استخدام البيانات التي تم الحصول عليها من EIS لترتيب أنظمة الطلاء المختارة المختلفة وفقا لأعلى مستوى من أداء الطلاء في محلول کلوريد الصوديوم وسطح الطلاء الخالي من اي آثار للتآکل أو الصدأ. وقد أشارت النتائج الکلية أن أفضل أداء من حيث الترتيب تم الحصول عليها ل ZE> S2> C | ||||
|